LiFeSnO4 Lacorre P, Hervieu M, Pannetier J, Choisnet J, Raveau B Journal of Solid State Chemistry 50 (1983) 196-203 Neutron diffraction study of Li1+x (Li2x/3 Fe1-x Sn1+x/3) O4, a nonstoichiometric ramsdellite and its transition to a double hexagonal close packed structure for x = 0 _cod_database_code 1000432 _database_code_amcsd 0013515 CELL PARAMETERS: 3.0660 5.0660 9.8740 90.000 90.000 90.000 SPACE GROUP: Pmcn X-RAY WAVELENGTH: 1.541838 Cell Volume: 153.366 Density (g/cm3): 5.315 MAX. ABS. INTENSITY / VOLUME**2: 92.17619998 RIR: 5.647 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 17.97 5.31 4.9370 0 0 2 2 19.70 100.00 4.5074 0 1 1 4 25.19 1.13 3.5357 0 1 2 4 32.44 48.81 2.7600 0 1 3 4 34.43 34.02 2.6046 1 0 2 4 35.41 48.70 2.5351 1 1 1 8 35.44 11.33 2.5330 0 2 0 2 36.40 10.06 2.4685 0 0 4 2 38.88 7.55 2.3164 1 1 2 8 40.01 1.11 2.2537 0 2 2 4 40.66 1.63 2.2191 0 1 4 4 44.15 10.23 2.0513 1 1 3 8 45.17 1.10 2.0074 0 2 3 4 47.27 3.83 1.9228 1 0 4 4 50.24 37.59 1.8159 1 2 2 8 51.71 16.36 1.7679 0 2 4 4 54.65 1.85 1.6794 1 2 3 8 55.18 2.40 1.6645 0 3 1 4 55.87 1.73 1.6457 0 0 6 2 58.50 19.20 1.5777 1 1 5 8 60.38 7.49 1.5330 2 0 0 2 60.45 2.75 1.5315 1 2 4 8 61.74 6.17 1.5025 0 3 3 4 63.61 10.90 1.4628 1 3 1 8 64.17 5.74 1.4514 2 1 1 8 64.24 8.43 1.4500 1 0 6 4 67.92 2.11 1.3800 0 2 6 4 69.13 4.74 1.3589 0 1 7 4 69.70 1.83 1.3492 1 3 3 8 70.23 7.93 1.3402 2 1 3 8 72.00 2.70 1.3115 2 2 0 4 72.59 2.38 1.3023 2 0 4 4 74.99 2.24 1.2665 0 4 0 2 75.56 2.66 1.2584 1 2 6 8 81.26 3.75 1.1839 1 3 5 8 83.46 5.94 1.1582 2 2 4 8 84.65 1.45 1.1450 1 0 8 4 85.20 4.04 1.1390 1 4 2 8 86.26 1.18 1.1276 2 3 1 8 86.34 1.59 1.1268 0 4 4 4 88.02 1.19 1.1095 0 2 8 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.