F8 Fe3 H4 O2 Leblanc M, Ferey G, Calage Y, De Pape R Journal of Solid State Chemistry 53 (1984) 360-368 Idle spin behavior of the shifted hexagonal tungsten bronze type compounds Fe Fe2 F8 (H2O)2 and Mn Fe2 F8 (H2O)2 _cod_database_code 1000193 _database_code_amcsd 0013528 CELL PARAMETERS: 7.6090 7.5140 7.4530 90.000 118.210 90.000 SPACE GROUP: C2/m X-RAY WAVELENGTH: 1.541838 Cell Volume: 375.504 Density (g/cm3): 3.182 MAX. ABS. INTENSITY / VOLUME**2: 20.23353109 RIR: 2.070 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.48 39.07 6.5677 0 0 1 2 17.73 32.72 5.0029 1 1 0 4 18.11 20.79 4.8989 -1 1 1 4 23.40 79.25 3.8010 -2 0 1 2 23.68 10.14 3.7570 0 2 0 2 25.92 15.66 3.4380 1 1 1 4 26.59 11.76 3.3526 2 0 0 2 26.71 6.39 3.3380 -1 1 2 4 27.15 56.58 3.2839 0 0 2 2 27.35 100.00 3.2611 0 2 1 4 27.61 3.95 3.2304 -2 0 2 2 33.54 12.75 2.6720 -2 2 1 4 35.90 6.13 2.5014 2 2 0 4 36.34 1.25 2.4725 0 2 2 4 36.69 1.51 2.4494 -2 2 2 4 36.93 4.12 2.4339 -2 0 3 2 37.70 1.19 2.3862 1 1 2 4 37.81 2.24 2.3791 -3 1 1 4 38.38 17.20 2.3452 -3 1 2 4 41.24 6.32 2.1892 0 0 3 2 42.18 6.21 2.1423 3 1 0 4 43.03 14.99 2.1021 1 3 1 4 43.73 3.87 2.0702 -3 1 3 4 47.00 2.02 1.9332 2 0 2 2 47.86 24.77 1.9005 -4 0 2 2 48.10 30.15 1.8915 0 2 3 4 48.46 20.11 1.8785 0 4 0 2 48.89 3.34 1.8629 -2 0 4 2 49.34 1.59 1.8468 -4 0 1 2 50.54 1.43 1.8061 0 4 1 4 51.10 4.98 1.7874 1 1 3 4 51.48 1.81 1.7752 1 3 2 4 52.14 1.14 1.7541 -1 1 4 4 52.22 2.28 1.7517 -1 3 3 4 52.68 2.10 1.7376 -3 1 4 4 53.29 5.53 1.7190 2 2 2 4 54.08 2.28 1.6959 -4 2 2 4 54.49 9.49 1.6841 -2 4 1 4 54.76 4.66 1.6763 4 0 0 2 55.02 6.44 1.6690 -2 2 4 4 55.07 3.48 1.6676 3 3 0 4 55.44 17.17 1.6574 -4 2 1 4 56.01 10.02 1.6419 0 0 4 2 56.12 3.05 1.6388 2 4 0 4 56.34 3.48 1.6330 -3 3 3 4 56.43 13.35 1.6306 0 4 2 4 56.56 6.46 1.6270 -4 2 3 4 56.68 2.33 1.6239 -2 4 2 4 57.02 5.88 1.6152 -4 0 4 2 60.45 2.39 1.5314 2 0 3 2 61.39 2.12 1.5102 2 4 1 4 61.47 1.51 1.5085 3 1 2 4 61.65 1.88 1.5045 0 2 4 4 62.06 1.33 1.4954 3 3 1 4 62.45 3.85 1.4871 -2 4 3 4 62.58 2.93 1.4844 -2 0 5 2 62.64 3.33 1.4830 1 3 3 4 63.43 2.46 1.4664 1 5 0 4 64.03 2.10 1.4542 -3 3 4 4 64.22 1.66 1.4503 -3 1 5 4 65.82 1.16 1.4188 1 1 4 4 65.86 1.96 1.4181 2 2 3 4 66.52 2.36 1.4057 -4 0 5 2 68.71 8.84 1.3662 4 2 1 4 70.48 7.92 1.3360 -4 4 2 4 71.30 1.20 1.3228 -2 4 4 4 71.69 5.35 1.3166 -4 2 5 4 73.82 3.39 1.2836 -3 5 2 4 74.55 2.25 1.2729 -3 3 5 4 74.77 3.58 1.2696 4 0 2 2 74.96 1.48 1.2670 -6 0 3 2 75.55 1.61 1.2586 -5 3 1 4 76.10 3.51 1.2507 4 4 0 4 76.89 2.51 1.2399 0 2 5 4 77.16 4.30 1.2363 0 4 4 4 77.61 2.81 1.2302 0 6 1 4 78.02 3.80 1.2247 -4 4 4 4 78.61 2.09 1.2170 -4 0 6 2 79.72 1.05 1.2028 4 2 2 4 81.01 1.48 1.1869 2 4 3 4 82.63 1.01 1.1677 -2 6 2 4 82.90 2.23 1.1646 -2 4 5 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.