Magnetite Fleet M E Journal of Solid State Chemistry 62 (1986) 75-82 The structure of magnetite: Symmetry of cubic spinels Note: Sample 633,MT1B, annealed at 1373 K Locality: Natural, not provided _database_code_amcsd 0020589 CELL PARAMETERS: 8.3969 8.3969 8.3969 90.000 90.000 90.000 SPACE GROUP: Fd3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 592.048 Density (g/cm3): 5.194 MAX. ABS. INTENSITY / VOLUME**2: 92.21779091 RIR: 5.781 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.30 7.95 4.8480 1 1 1 8 30.10 28.13 2.9688 2 2 0 12 35.46 100.00 2.5318 3 1 1 24 37.09 8.20 2.4240 2 2 2 8 43.09 20.19 2.0992 4 0 0 6 53.46 9.56 1.7140 4 2 2 24 56.99 24.89 1.6160 5 1 1 24 56.99 6.36 1.6160 3 3 3 8 62.58 41.77 1.4844 4 4 0 12 70.99 3.51 1.3277 6 2 0 24 74.03 8.76 1.2805 5 3 3 24 75.03 3.84 1.2659 6 2 2 24 79.00 2.65 1.2120 4 4 4 8 86.79 3.89 1.1221 6 4 2 48 89.69 5.49 1.0932 5 5 3 24 89.69 8.80 1.0932 7 3 1 48 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.