Tapiolite-(Fe) Eicher S M, Greedan J E, Lushington K J Journal of Solid State Chemistry 62 (1986) 220-230 The magnetic properties of FeTa2O6. Magnetic structure and low-dimensional behavior Locality: synthetic _database_code_amcsd 0013576 CELL PARAMETERS: 4.7490 4.7490 9.1920 90.000 90.000 90.000 SPACE GROUP: P4_2/mnm X-RAY WAVELENGTH: 1.541838 Cell Volume: 207.307 Density (g/cm3): 8.229 MAX. ABS. INTENSITY / VOLUME**2: 311.4547979 RIR: 12.324 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 19.31 9.54 4.5960 0 0 2 2 21.06 28.03 4.2192 1 0 1 8 26.54 100.00 3.3581 1 1 0 4 33.04 9.18 2.7114 1 1 2 8 34.85 80.50 2.5746 1 0 3 8 37.89 24.67 2.3745 2 0 0 4 39.20 1.03 2.2980 0 0 4 2 39.83 2.60 2.2634 1 1 3 8 42.87 4.11 2.1096 2 0 2 8 43.75 8.34 2.0693 2 1 1 16 47.97 3.09 1.8965 1 1 4 8 52.42 62.59 1.7455 2 1 3 16 53.44 2.50 1.7144 1 0 5 8 54.66 15.80 1.6790 2 2 0 4 55.66 2.45 1.6513 2 0 4 8 58.53 2.14 1.5771 2 2 2 8 59.23 1.64 1.5600 3 0 1 8 60.43 6.22 1.5320 0 0 6 2 61.77 15.37 1.5018 3 1 0 8 65.37 2.82 1.4275 3 1 2 16 66.48 17.29 1.4064 3 0 3 8 67.16 13.32 1.3938 1 1 6 8 67.37 2.72 1.3900 2 1 5 16 72.50 2.10 1.3038 3 2 1 16 73.58 7.45 1.2873 2 0 6 8 75.65 1.86 1.2571 3 1 4 16 79.15 12.68 1.2101 3 2 3 16 80.98 4.03 1.1873 4 0 0 4 84.84 1.33 1.1429 4 1 1 16 85.88 7.56 1.1317 2 2 6 8 87.06 3.71 1.1194 3 3 0 4 87.30 1.10 1.1169 2 1 7 16 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.