Srilankite Bordet P, McHale A, Santoro A, Roth R Journal of Solid State Chemistry 64 (1986) 30-46 Powder neutron diffraction study of ZrTiO4, Zr5Ti7O24, and FeNb2O6 Locality: synthetic _cod_database_code 1008790 _database_code_amcsd 0016662 CELL PARAMETERS: 4.8042 5.4825 5.0313 90.000 90.000 90.000 SPACE GROUP: Pbcn X-RAY WAVELENGTH: 1.541838 Cell Volume: 132.520 Density (g/cm3): 5.089 MAX. ABS. INTENSITY / VOLUME**2: 107.1595440 RIR: 6.857 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 24.64 1.98 3.6132 1 1 0 4 30.46 100.00 2.9348 1 1 1 8 32.67 14.90 2.7413 0 2 0 2 35.69 8.06 2.5157 0 0 2 2 37.44 4.30 2.4021 2 0 0 2 40.48 2.75 2.2286 1 0 2 4 41.98 5.99 2.1521 1 2 1 8 49.16 13.69 1.8535 0 2 2 4 50.52 13.47 1.8066 2 2 0 4 52.69 15.00 1.7373 2 0 2 4 53.92 2.12 1.7003 2 2 1 8 56.93 14.02 1.6174 1 3 1 8 60.90 12.04 1.5212 1 1 3 8 63.26 10.68 1.4701 3 1 1 8 63.38 8.28 1.4674 2 2 2 8 65.21 1.27 1.4306 0 2 3 4 75.60 1.18 1.2578 0 0 4 2 79.66 2.79 1.2036 0 4 2 4 79.86 1.90 1.2011 4 0 0 2 80.21 3.79 1.1967 1 3 3 8 80.72 3.13 1.1905 2 4 0 4 82.32 3.43 1.1713 3 3 1 8 84.81 1.90 1.1432 0 2 4 4 85.74 3.16 1.1332 3 1 3 8 87.55 1.95 1.1143 2 0 4 4 88.98 1.35 1.1001 4 2 0 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.