Er Fe2 H3.45 Fruchart D, Berthier Y, De Saxce T, Vulliet P Journal of Solid State Chemistry 67 (1987) 197-209 Etudes structurales et magnetiques de formes cubiques et rhomboedriques Ln Fe2 Hx, Ln=Er,Tb _cod_database_code 1008877 _database_code_amcsd 0016744 CELL PARAMETERS: 7.8150 7.8150 7.8150 91.200 91.200 91.200 SPACE GROUP: R-3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 476.977 Density (g/cm3): 7.852 MAX. ABS. INTENSITY / VOLUME**2: 195.5638576 RIR: 8.110 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 11.33 1.26 7.8115 1 0 0 6 15.87 1.29 5.5836 0 -1 1 6 16.22 1.60 5.4654 1 1 0 6 19.54 19.90 4.5425 1 -1 1 6 20.11 13.14 4.4165 1 1 1 2 22.77 1.09 3.9057 2 0 0 6 27.88 1.69 3.2005 2 -1 1 12 32.06 63.84 2.7918 0 -2 2 6 32.77 57.64 2.7327 2 2 0 6 35.11 1.13 2.5557 2 2 1 6 37.82 37.74 2.3785 -1 -1 3 6 38.13 100.00 2.3598 3 -1 1 12 38.75 25.63 2.3238 3 1 1 6 39.68 11.94 2.2712 2 -2 2 6 40.87 8.53 2.2082 2 2 2 2 46.50 2.44 1.9529 4 0 0 6 50.40 3.85 1.8105 3 -3 1 12 51.87 4.09 1.7626 3 3 1 6 52.86 2.72 1.7319 4 2 0 12 57.15 10.11 1.6118 2 -4 2 6 57.60 16.14 1.6002 4 -2 2 12 58.95 9.58 1.5668 4 2 2 6 61.21 11.60 1.5142 3 -3 3 6 61.21 9.30 1.5142 -1 -1 5 6 61.65 12.88 1.5045 5 -1 1 12 62.30 9.45 1.4904 5 1 1 6 67.05 15.07 1.3959 0 -4 4 6 68.70 11.67 1.3664 4 4 0 6 70.59 1.26 1.3343 -1 -3 5 12 70.79 2.79 1.3310 5 -3 1 12 71.80 3.91 1.3148 5 -1 3 12 76.65 6.17 1.2431 0 -2 6 12 77.83 5.38 1.2273 6 2 0 12 79.64 2.50 1.2039 3 -5 3 6 80.22 3.77 1.1966 5 -3 3 12 81.59 4.02 1.1799 6 -2 2 12 82.54 3.91 1.1688 5 3 3 6 89.58 1.39 1.0943 7 -1 1 12 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.