Fe12 O19 Sr Obradors X, Solans X, Collomb A, Samaras D, Rodriguez J, Pernet M, Font-Altaba M Journal of Solid State Chemistry 72 (1988) 218-224 Crystal structure of strontium hexaferrite Sr Fe12 O19 _cod_database_code 1006000 _database_code_amcsd 0013608 CELL PARAMETERS: 5.8844 5.8844 23.0500 90.000 90.000 120.000 SPACE GROUP: P6_3/mmc X-RAY WAVELENGTH: 1.541838 Cell Volume: 691.203 Density (g/cm3): 5.101 MAX. ABS. INTENSITY / VOLUME**2: 36.43295503 RIR: 2.326 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 7.67 1.63 11.5250 0 0 2 2 15.38 2.07 5.7625 0 0 4 2 19.04 5.83 4.6607 1 0 2 12 20.92 3.61 4.2468 1 0 3 12 23.15 6.40 3.8417 0 0 6 2 29.11 3.27 3.0677 1 0 6 12 30.38 42.17 2.9422 1 1 0 6 31.04 14.70 2.8812 0 0 8 2 31.38 3.86 2.8508 1 1 2 12 32.37 87.11 2.7657 1 0 7 12 34.22 100.00 2.6204 1 1 4 12 35.22 9.17 2.5480 2 0 0 6 35.44 13.72 2.5326 2 0 1 12 35.80 13.15 2.5081 1 0 8 12 36.10 2.86 2.4879 2 0 2 12 37.18 43.69 2.4185 2 0 3 12 38.54 7.15 2.3359 1 1 6 12 38.64 1.03 2.3304 2 0 4 12 40.45 26.13 2.2301 2 0 5 12 42.58 16.81 2.1234 2 0 6 12 44.98 1.97 2.0152 2 0 7 12 46.88 3.61 1.9380 1 0 11 12 50.28 1.36 1.8145 1 1 10 12 50.53 4.27 1.8063 2 0 9 12 50.80 1.55 1.7974 1 0 12 12 53.20 1.59 1.7218 2 1 6 24 53.62 5.01 1.7094 2 0 10 12 53.98 6.82 1.6987 3 0 0 6 55.25 33.96 1.6626 2 1 7 24 55.84 6.13 1.6464 0 0 14 2 56.48 19.77 1.6294 3 0 4 12 56.89 45.07 1.6185 2 0 11 12 57.28 2.77 1.6084 1 1 12 12 57.56 9.00 1.6013 2 1 8 24 59.50 1.71 1.5536 3 0 6 12 60.35 5.55 1.5338 2 0 12 12 63.20 1.14 1.4712 1 0 15 12 63.21 44.68 1.4711 2 2 0 6 63.97 3.76 1.4554 2 0 13 12 65.86 2.38 1.4181 2 1 11 24 67.76 9.74 1.3829 2 0 14 12 68.27 1.23 1.3738 2 2 6 12 69.06 1.46 1.3601 2 1 12 24 72.08 1.11 1.3103 1 0 17 12 72.09 5.68 1.3102 2 2 8 12 72.82 12.03 1.2988 3 1 7 24 73.14 1.85 1.2939 1 1 16 12 74.58 1.06 1.2725 3 0 12 12 74.61 1.47 1.2721 4 0 1 12 74.82 2.20 1.2689 3 1 8 24 75.67 4.14 1.2568 4 0 3 12 76.74 1.99 1.2419 1 0 18 12 77.78 1.92 1.2280 4 0 5 12 79.21 1.33 1.2092 4 0 6 12 79.85 1.01 1.2012 2 1 15 24 80.19 1.04 1.1970 2 0 17 12 82.08 5.47 1.1742 1 1 18 12 82.28 1.11 1.1718 3 1 11 24 83.97 1.21 1.1525 0 0 20 2 88.81 2.07 1.1017 3 2 7 24 89.30 7.42 1.0970 2 2 14 12 89.83 2.77 1.0919 4 1 4 24 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.