In0.12 Li1.12 O12 P3 Ti1.88 Tran Q, Hamdoune S, Soubeyroux J, Prince E Journal of Solid State Chemistry 72 (1988) 309-315 Neutron powder diffraction study of solid solution Li1+x Ti2-x Inx P3 O12 _cod_database_code 1008366 _database_code_amcsd 0016276 CELL PARAMETERS: 8.5476 8.5476 20.9512 90.000 90.000 120.000 SPACE GROUP: R-3c X-RAY WAVELENGTH: 1.541838 Cell Volume: 1325.647 Density (g/cm3): 2.980 MAX. ABS. INTENSITY / VOLUME**2: 22.98570252 RIR: 2.512 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 14.65 24.70 6.0454 0 1 2 6 20.77 43.45 4.2757 1 0 4 6 20.78 28.44 4.2738 1 1 0 6 24.42 100.00 3.6454 1 1 3 12 25.51 4.22 3.4919 0 0 6 2 25.52 1.30 3.4898 2 0 2 6 29.55 29.85 3.0227 0 2 4 6 32.28 14.56 2.7732 2 1 1 12 33.13 29.66 2.7041 1 1 6 12 36.41 10.49 2.4678 2 1 4 12 36.41 14.63 2.4675 3 0 0 6 42.27 1.75 2.1378 2 0 8 6 44.31 5.47 2.0443 1 1 9 12 44.32 1.53 2.0439 2 1 7 12 44.33 2.74 2.0434 2 2 3 12 47.56 13.44 1.9120 1 2 8 12 47.57 4.22 1.9115 1 3 4 12 49.44 3.22 1.8437 3 1 5 12 50.03 1.41 1.8233 0 2 10 6 50.04 10.16 1.8227 2 2 6 12 50.05 4.03 1.8224 0 4 2 6 52.41 2.00 1.7459 0 0 12 2 54.17 4.31 1.6930 1 3 7 12 54.73 7.95 1.6770 2 1 10 12 56.98 1.68 1.6163 1 1 12 12 57.00 6.41 1.6158 3 1 8 12 57.01 5.97 1.6154 3 2 4 12 57.01 8.95 1.6153 4 1 0 12 58.64 1.45 1.5742 2 2 9 12 58.66 1.64 1.5739 2 3 5 12 58.66 2.10 1.5738 4 1 3 12 58.66 1.65 1.5738 1 4 3 12 61.34 2.69 1.5114 0 4 8 6 62.92 1.48 1.4770 3 2 7 12 63.41 1.44 1.4668 0 1 14 6 63.43 4.78 1.4664 1 3 10 12 63.45 2.36 1.4661 1 4 6 12 63.45 2.35 1.4661 4 1 6 12 65.51 1.18 1.4249 2 3 8 12 65.52 2.76 1.4247 0 5 4 6 65.52 1.64 1.4246 3 3 0 6 67.02 1.54 1.3963 3 1 11 12 67.51 2.51 1.3874 2 0 14 6 67.53 2.60 1.3870 4 0 10 6 69.53 1.80 1.3520 2 2 12 12 69.56 1.79 1.3516 2 4 4 12 70.99 3.24 1.3276 1 1 15 12 71.04 2.06 1.3268 5 1 1 12 71.49 2.30 1.3196 1 2 14 12 71.51 1.01 1.3193 3 2 10 12 73.49 4.36 1.2887 5 1 4 12 74.94 1.62 1.2673 1 5 5 12 77.34 5.23 1.2337 6 0 0 6 78.76 1.76 1.2150 5 1 7 12 82.96 2.19 1.1640 0 0 18 2 86.73 2.20 1.1228 2 3 14 12 88.62 1.05 1.1036 3 4 8 12 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.