Be K O4 P Masse R, Durif A Journal of Solid State Chemistry 73 (1988) 468-472 Contribution to the Crystal Chemistry of M(I) M(II) P O4 Monophosphates (M(I) = K, Rb, Cs; M(II) = Be) _cod_database_code 1007182 _database_code_amcsd 0013613 CELL PARAMETERS: 8.5060 4.9370 8.3440 90.000 90.000 90.000 SPACE GROUP: Pc2_1n X-RAY WAVELENGTH: 1.541838 Cell Volume: 350.399 Density (g/cm3): 2.712 MAX. ABS. INTENSITY / VOLUME**2: 10.41155435 RIR: 1.250 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 14.87 30.37 5.9565 1 0 1 4 21.30 11.14 4.1720 0 0 2 2 23.40 37.48 3.8011 1 1 1 4 23.48 16.01 3.7892 2 0 1 4 28.00 6.35 3.1866 0 1 2 2 29.72 76.62 3.0059 2 1 1 4 29.94 100.00 2.9841 1 1 2 4 30.00 49.35 2.9783 2 0 2 4 33.38 7.65 2.6846 3 0 1 4 33.91 7.46 2.6436 1 0 3 4 35.19 2.45 2.5502 2 1 2 4 36.40 26.72 2.4685 0 2 0 1 36.55 46.23 2.4587 3 1 0 2 38.39 3.29 2.3450 3 0 2 4 38.63 1.85 2.3305 1 1 3 4 39.52 3.52 2.2804 1 2 1 4 42.33 8.33 2.1349 2 2 0 2 42.51 1.19 2.1265 4 0 0 2 42.55 20.48 2.1245 0 2 2 2 42.69 23.81 2.1182 3 1 2 4 43.38 28.25 2.0860 0 0 4 2 43.77 4.97 2.0683 2 2 1 4 43.94 1.33 2.0606 4 0 1 4 45.69 2.40 1.9855 3 0 3 4 47.31 1.14 1.9215 0 1 4 2 47.86 1.47 1.9006 2 2 2 4 48.57 2.29 1.8743 1 1 4 4 50.21 3.70 1.8171 3 2 1 4 50.59 4.52 1.8042 1 2 3 4 52.24 1.77 1.7511 2 1 4 4 53.93 2.12 1.7002 3 2 2 4 54.62 1.33 1.6802 3 0 4 4 55.10 9.01 1.6669 5 0 1 4 56.17 2.38 1.6376 1 0 5 4 57.00 1.56 1.6157 1 3 0 2 57.17 1.00 1.6111 4 2 0 2 57.28 1.23 1.6084 5 1 0 2 57.67 10.78 1.5983 4 1 3 4 57.87 3.16 1.5933 0 2 4 2 57.98 5.80 1.5907 3 1 4 4 58.16 1.58 1.5862 1 3 1 4 58.33 1.65 1.5819 4 2 1 4 58.44 1.12 1.5793 5 1 1 4 59.77 1.76 1.5471 3 2 3 4 61.42 5.72 1.5095 2 3 1 4 61.55 6.27 1.5067 1 3 2 4 61.72 3.91 1.5029 4 2 2 4 61.82 3.18 1.5007 5 1 2 4 62.22 7.55 1.4920 2 2 4 4 62.36 1.69 1.4891 4 0 4 4 62.70 10.91 1.4819 2 1 5 4 65.59 11.05 1.4233 3 3 0 2 65.88 2.81 1.4177 6 0 0 2 67.42 1.40 1.3890 3 2 4 4 67.84 7.79 1.3814 5 2 1 4 68.80 2.47 1.3646 1 2 5 4 69.96 1.88 1.3448 6 1 1 4 74.25 1.79 1.2774 1 3 4 4 77.31 2.97 1.2342 0 4 0 1 77.67 2.27 1.2294 6 2 0 2 78.10 1.26 1.2236 6 1 3 4 79.03 5.69 1.2116 0 2 6 2 79.12 8.31 1.2105 3 1 6 4 80.65 3.86 1.1913 5 0 5 4 81.35 1.04 1.1828 5 3 0 2 81.59 2.02 1.1799 7 1 0 2 81.69 3.31 1.1788 4 3 3 4 81.95 3.30 1.1757 3 3 4 4 82.58 1.14 1.1683 7 1 1 4 85.08 4.66 1.1402 2 4 2 4 85.29 2.07 1.1380 5 3 2 4 86.07 3.79 1.1297 2 3 5 4 87.57 1.03 1.1142 3 2 6 4 87.63 1.67 1.1135 7 0 3 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.