Li2 Mn O3 Strobel P, Lambert-Andron B Journal of Solid State Chemistry 75 (1988) 90-98 Crystallographic and Magnetic Structure of Li2 Mn O3 _cod_database_code 1008373 _database_code_amcsd 0016283 CELL PARAMETERS: 4.9370 8.5320 5.0300 90.000 109.460 90.000 SPACE GROUP: C2/m X-RAY WAVELENGTH: 1.541838 Cell Volume: 199.773 Density (g/cm3): 3.883 MAX. ABS. INTENSITY / VOLUME**2: 32.12959717 RIR: 2.694 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.71 100.00 4.7427 0 0 1 2 20.82 19.41 4.2660 0 2 0 2 21.75 32.90 4.0863 1 1 0 4 24.24 23.50 3.6720 -1 1 1 4 28.13 14.80 3.1717 0 2 1 4 32.85 7.49 2.7264 1 1 1 4 36.92 10.52 2.4347 -2 0 1 2 37.04 21.45 2.4269 1 3 0 4 37.89 3.99 2.3745 -1 1 2 4 37.94 1.73 2.3713 0 0 2 2 38.63 3.03 2.3309 -1 3 1 4 38.69 1.49 2.3275 2 0 0 2 42.76 1.88 2.1146 -2 2 1 4 43.67 2.60 2.0726 0 2 2 4 44.33 2.14 2.0432 2 2 0 4 44.55 30.68 2.0340 -2 0 2 2 44.81 60.45 2.0227 1 3 1 4 46.69 2.35 1.9453 0 4 1 4 48.81 5.80 1.8658 -1 3 2 4 49.01 2.93 1.8588 2 0 1 2 49.66 2.72 1.8360 -2 2 2 4 49.78 1.73 1.8316 1 1 2 4 53.80 2.59 1.7041 2 2 1 4 55.89 1.16 1.6452 -1 1 3 4 56.99 1.31 1.6159 -3 1 1 4 57.52 1.91 1.6021 1 5 0 4 58.17 2.22 1.5858 0 4 2 4 58.37 1.01 1.5809 0 0 3 2 58.65 4.23 1.5740 -2 0 3 2 58.71 2.04 1.5725 2 4 0 4 59.00 8.18 1.5656 1 3 2 4 60.41 2.01 1.5324 -3 1 2 4 62.94 1.78 1.4767 -2 2 3 4 63.37 1.63 1.4677 1 5 1 4 64.52 14.24 1.4443 -1 3 3 4 64.80 7.08 1.4387 2 0 2 2 65.54 13.87 1.4244 -3 3 1 4 65.66 6.87 1.4220 0 6 0 2 66.75 1.11 1.4014 2 4 1 4 68.70 3.57 1.3662 -3 3 2 4 68.88 1.03 1.3632 2 2 2 4 68.94 3.41 1.3621 3 3 0 4 68.94 3.47 1.3621 0 6 1 4 77.78 1.72 1.2279 -2 6 1 4 81.11 2.81 1.1857 0 0 4 2 82.83 5.54 1.1654 -2 6 2 4 82.97 2.79 1.1637 4 0 0 2 84.48 2.67 1.1468 -1 3 4 4 84.85 1.31 1.1427 2 0 3 2 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.