Ag Mo Na O4 Rulmont A, Tarte P, Foumakoye G, Fransolet A, Choisnet J Journal of Solid State Chemistry 76 (1988) 18-25 The disordered Spinel Na Ag Mo O4 and Its High Temperature, Ordered Orthorhombic Polymorph _cod_database_code 1001372 _database_code_amcsd 0013621 CELL PARAMETERS: 10.3840 7.1220 5.5933 90.000 90.000 90.000 SPACE GROUP: Pnma X-RAY WAVELENGTH: 1.541838 Cell Volume: 413.652 Density (g/cm3): 4.669 MAX. ABS. INTENSITY / VOLUME**2: 52.40482401 RIR: 3.655 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 17.08 20.95 5.1920 2 0 0 2 18.01 60.59 4.9244 1 0 1 4 21.18 2.57 4.1955 2 1 0 4 21.94 5.72 4.0504 1 1 1 8 25.01 62.01 3.5610 0 2 0 2 30.37 100.00 2.9433 3 0 1 4 30.44 34.98 2.9367 2 2 0 4 30.99 53.32 2.8856 1 2 1 8 32.00 51.51 2.7966 0 0 2 2 32.93 23.26 2.7202 3 1 1 8 33.18 1.75 2.7004 1 0 2 4 34.49 7.21 2.6001 2 2 1 8 34.55 15.13 2.5960 4 0 0 2 36.49 4.12 2.4622 2 0 2 4 36.85 4.15 2.4390 4 1 0 4 38.69 6.89 2.3270 2 1 2 8 39.73 31.34 2.2687 3 2 1 8 41.04 27.52 2.1994 0 2 2 4 41.84 2.81 2.1590 2 3 0 4 43.12 14.79 2.0977 4 2 0 4 44.75 18.30 2.0252 2 2 2 8 47.81 3.21 1.9026 4 0 2 4 48.47 1.69 1.8780 5 1 1 8 49.32 9.66 1.8478 3 3 1 8 49.59 2.45 1.8382 4 1 2 8 49.68 2.34 1.8351 1 0 3 4 51.31 16.72 1.7805 0 4 0 2 52.21 1.45 1.7519 4 3 0 4 52.90 6.53 1.7307 6 0 0 2 53.63 2.09 1.7090 2 3 2 8 53.65 5.59 1.7083 5 2 1 8 54.48 1.55 1.6842 2 4 0 4 54.57 6.87 1.6817 6 1 0 4 54.70 12.58 1.6781 4 2 2 8 54.83 4.12 1.6744 1 4 1 8 56.02 13.66 1.6415 3 0 3 4 56.41 14.80 1.6312 1 2 3 8 57.63 4.22 1.5995 3 1 3 8 59.37 4.20 1.5566 6 2 0 4 60.80 20.10 1.5234 3 4 1 8 61.61 1.38 1.5054 5 3 1 8 61.77 12.28 1.5019 0 4 2 4 62.28 13.55 1.4907 3 2 3 8 62.56 1.18 1.4847 4 3 2 8 63.18 5.37 1.4717 6 0 2 4 63.34 2.70 1.4683 4 4 0 4 64.60 1.35 1.4428 2 4 2 8 64.68 10.54 1.4412 6 1 2 8 66.52 5.20 1.4057 7 1 1 8 66.91 4.89 1.3985 6 3 0 4 66.91 3.76 1.3983 0 0 4 2 69.06 3.40 1.3601 6 2 2 8 69.64 1.52 1.3501 3 3 3 8 70.85 2.08 1.3301 7 2 1 8 72.64 5.29 1.3016 0 2 4 4 72.74 1.61 1.3000 4 4 2 8 73.92 1.33 1.2822 3 5 1 8 74.21 1.59 1.2779 1 4 3 8 75.27 2.85 1.2625 2 2 4 8 76.10 5.95 1.2508 6 3 2 8 76.81 3.36 1.2410 6 4 0 4 77.82 3.76 1.2274 7 3 1 8 79.40 8.70 1.2068 3 4 3 8 81.00 2.01 1.1870 0 6 0 2 82.99 4.07 1.1635 4 2 4 8 83.55 1.17 1.1571 2 6 0 4 83.84 2.74 1.1539 1 6 1 8 84.58 2.48 1.1457 7 1 3 8 85.63 3.83 1.1343 6 4 2 8 87.38 5.09 1.1160 9 1 1 8 88.61 2.03 1.1037 7 2 3 8 88.90 3.23 1.1009 3 6 1 8 89.01 1.12 1.0998 6 5 0 4 89.02 3.50 1.0997 0 4 4 4 89.75 2.23 1.0927 0 6 2 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.