Fe O6 Ru Sr2 Battle P, Gibb T, Jones C, Studer F Journal of Solid State Chemistry 78 (1989) 281-293 Spin-Glass Behavior in Sr2 Fe Ru O6 and Ba La Ni Ru O6: A Comparison with Antiferromagnetic Ba La Zn Ru O6 _cod_database_code 1001400 _database_code_amcsd 0013641 CELL PARAMETERS: 5.5092 5.5138 7.8752 90.000 90.130 90.000 SPACE GROUP: I2/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 239.221 Density (g/cm3): 5.943 MAX. ABS. INTENSITY / VOLUME**2: 67.02200597 RIR: 3.672 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 22.82 1.58 3.8972 1 1 0 4 32.29 99.12 2.7721 -1 1 2 4 32.35 100.00 2.7677 1 1 2 4 32.48 50.96 2.7569 0 2 0 2 32.50 51.37 2.7546 2 0 0 2 39.90 2.89 2.2595 -2 0 2 2 39.92 6.20 2.2584 0 2 2 4 39.99 3.14 2.2547 2 0 2 2 46.10 33.81 1.9688 0 0 4 2 46.61 63.11 1.9486 2 2 0 4 57.47 8.71 1.6035 -2 0 4 2 57.52 16.80 1.6022 0 2 4 4 57.61 8.21 1.6000 2 0 4 2 57.82 16.90 1.5946 -1 3 2 4 57.82 16.70 1.5946 -3 1 2 4 57.86 16.36 1.5938 1 3 2 4 57.92 16.44 1.5920 3 1 2 4 67.59 15.69 1.3861 -2 2 4 4 67.71 16.13 1.3838 2 2 4 4 68.01 7.65 1.3785 0 4 0 2 68.07 7.48 1.3773 4 0 0 2 76.55 5.90 1.2445 -1 1 6 4 76.64 6.05 1.2433 1 1 6 4 77.31 5.33 1.2343 -3 3 2 4 77.39 5.43 1.2331 3 3 2 4 77.42 6.31 1.2327 2 4 0 4 77.47 6.42 1.2321 4 2 0 4 86.06 3.22 1.1298 -4 0 4 2 86.11 6.76 1.1292 0 4 4 4 86.29 3.40 1.1274 4 0 4 2 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.