Ca2 N2 Zn Chern M, DiSalvo F Journal of Solid State Chemistry 88 (1990) 528-533 Synthesis, structure and properties of Ca2ZnN2 _cod_database_code 1005002 _database_code_amcsd 0013683 CELL PARAMETERS: 3.5835 3.5835 12.6583 90.000 90.000 90.000 SPACE GROUP: I4/mmm X-RAY WAVELENGTH: 1.541838 Cell Volume: 162.551 Density (g/cm3): 3.546 MAX. ABS. INTENSITY / VOLUME**2: 51.81835176 RIR: 4.758 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.99 5.35 6.3292 0 0 2 2 25.84 24.07 3.4480 1 0 1 8 32.79 100.00 2.7314 1 0 3 8 35.42 79.68 2.5339 1 1 0 4 38.26 2.69 2.3524 1 1 2 8 42.87 19.64 2.1097 0 0 6 2 43.78 2.97 2.0677 1 0 5 8 50.97 23.55 1.7917 2 0 0 4 53.12 1.18 1.7240 2 0 2 8 56.78 29.01 1.6213 1 1 6 8 57.05 2.52 1.6144 1 0 7 8 58.01 4.33 1.5899 2 1 1 16 61.94 25.61 1.4982 2 1 3 16 68.73 14.12 1.3657 2 0 6 8 69.41 1.51 1.3541 2 1 5 16 70.12 1.55 1.3421 1 1 8 8 72.15 8.66 1.3092 1 0 9 8 74.96 5.58 1.2670 2 2 0 4 80.00 1.61 1.1994 2 1 7 16 84.25 4.33 1.1493 3 0 3 8 85.73 7.14 1.1332 3 1 0 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.