Ge2 Li O12 P3 Alami M, Brochu R, Soubeyroux J, Gravereau P, Le Flem G, Hagenmueller P Journal of Solid State Chemistry 90 (1991) 185-193 Structure and thermal expansion of LiGe2(PO4)3 _cod_database_code 1008511 _database_code_amcsd 0016404 CELL PARAMETERS: 8.2722 8.2722 20.4825 90.000 90.000 120.000 SPACE GROUP: R-3c X-RAY WAVELENGTH: 1.541838 Cell Volume: 1213.824 Density (g/cm3): 3.588 MAX. ABS. INTENSITY / VOLUME**2: 23.80033781 RIR: 2.160 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 15.09 33.42 5.8703 0 1 2 6 21.33 98.86 4.1659 1 0 4 6 21.48 76.51 4.1361 1 1 0 6 25.17 100.00 3.5376 1 1 3 12 26.10 1.51 3.4137 0 0 6 2 30.46 65.61 2.9351 0 2 4 6 33.38 17.34 2.6844 2 1 1 12 34.05 43.12 2.6328 1 1 6 12 37.30 1.63 2.4110 0 1 8 6 37.58 26.53 2.3937 2 1 4 12 37.67 28.56 2.3880 3 0 0 6 43.45 5.47 2.0829 2 0 8 6 45.49 5.37 1.9939 1 1 9 12 45.65 1.50 1.9874 2 1 7 12 45.85 2.86 1.9792 2 2 3 12 46.09 3.21 1.9693 1 0 10 6 46.40 1.44 1.9568 0 3 6 6 46.56 2.65 1.9505 3 1 2 12 48.96 23.65 1.8603 1 2 8 12 49.19 13.98 1.8524 1 3 4 12 51.09 2.51 1.7877 3 1 5 12 51.39 4.69 1.7781 0 2 10 6 51.68 15.90 1.7688 2 2 6 12 51.82 5.84 1.7642 0 4 2 6 53.70 1.62 1.7069 0 0 12 2 55.94 4.67 1.6438 1 3 7 12 56.32 14.59 1.6335 2 1 10 12 58.50 3.32 1.5778 1 1 12 12 58.83 11.97 1.5697 3 1 8 12 59.03 13.29 1.5649 3 2 4 12 59.09 18.67 1.5633 4 1 0 12 60.49 1.02 1.5305 2 2 9 12 60.72 2.42 1.5253 2 3 5 12 60.78 2.62 1.5239 4 1 3 12 63.38 5.85 1.4676 0 4 8 6 65.07 3.40 1.4334 0 1 14 6 65.09 1.59 1.4330 3 2 7 12 65.44 10.36 1.4262 1 3 10 12 65.69 4.64 1.4214 1 4 6 12 65.69 4.56 1.4214 4 1 6 12 67.75 3.18 1.3831 2 3 8 12 67.93 5.65 1.3798 0 5 4 6 68.00 3.87 1.3787 3 3 0 6 69.14 1.44 1.3587 3 1 11 12 69.39 6.10 1.3544 2 0 14 6 69.75 5.16 1.3483 4 0 10 6 71.69 3.46 1.3164 2 2 12 12 72.17 4.99 1.3089 2 4 4 12 72.96 3.45 1.2967 1 1 15 12 73.59 6.45 1.2872 1 2 14 12 73.79 2.44 1.2841 5 1 1 12 73.94 2.98 1.2819 3 2 10 12 76.31 9.57 1.2479 5 1 4 12 77.81 1.45 1.2276 1 5 5 12 80.20 1.68 1.1968 4 2 8 12 80.43 7.07 1.1940 6 0 0 6 81.74 3.54 1.1781 3 1 14 12 81.77 2.24 1.1778 5 1 7 12 84.45 1.03 1.1471 5 2 0 12 85.29 3.31 1.1379 0 0 18 2 86.09 1.79 1.1294 2 4 10 12 89.28 1.68 1.0972 1 1 18 12 89.73 5.07 1.0928 2 3 14 12 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.