Ge2 Li O12 P3 Alami M, Brochu R, Soubeyroux J, Gravereau P, Le Flem G, Hagenmueller P Journal of Solid State Chemistry 90 (1991) 185-193 Structure and thermal expansion of LiGe2(PO4)3 _cod_database_code 1008512 _database_code_amcsd 0016405 CELL PARAMETERS: 8.2682 8.2682 20.4940 90.000 90.000 120.000 SPACE GROUP: R-3c X-RAY WAVELENGTH: 1.541838 Cell Volume: 1213.331 Density (g/cm3): 3.589 MAX. ABS. INTENSITY / VOLUME**2: 24.41305177 RIR: 2.215 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 15.09 29.92 5.8694 0 1 2 6 21.32 97.13 4.1667 1 0 4 6 21.49 71.59 4.1341 1 1 0 6 25.18 100.00 3.5369 1 1 3 12 26.09 1.97 3.4157 0 0 6 2 30.46 63.90 2.9347 0 2 4 6 33.40 17.00 2.6831 2 1 1 12 34.05 39.15 2.6332 1 1 6 12 37.28 2.01 2.4120 0 1 8 6 37.59 26.99 2.3931 2 1 4 12 37.69 28.67 2.3868 3 0 0 6 43.44 6.18 2.0834 2 0 8 6 45.48 5.11 1.9946 1 1 9 12 45.65 1.52 1.9874 2 1 7 12 45.87 2.63 1.9785 2 2 3 12 46.07 2.77 1.9703 1 0 10 6 46.41 1.08 1.9565 0 3 6 6 46.58 2.31 1.9497 3 1 2 12 48.96 25.00 1.8605 1 2 8 12 49.21 13.81 1.8517 1 3 4 12 51.11 2.49 1.7872 3 1 5 12 51.37 4.19 1.7786 0 2 10 6 51.69 14.72 1.7684 2 2 6 12 51.85 5.76 1.7634 0 4 2 6 53.67 1.24 1.7078 0 0 12 2 55.95 4.42 1.6435 1 3 7 12 56.31 13.85 1.6338 2 1 10 12 58.47 4.14 1.5784 1 1 12 12 58.84 12.14 1.5696 3 1 8 12 59.05 13.30 1.5643 3 2 4 12 59.13 18.44 1.5625 4 1 0 12 60.49 1.08 1.5305 2 2 9 12 60.74 2.11 1.5248 2 3 5 12 60.81 2.46 1.5232 4 1 3 12 63.39 5.67 1.4674 0 4 8 6 65.03 3.40 1.4342 0 1 14 6 65.11 1.32 1.4326 3 2 7 12 65.44 9.14 1.4262 1 3 10 12 65.71 4.26 1.4209 1 4 6 12 65.71 4.28 1.4209 4 1 6 12 67.77 3.43 1.3828 2 3 8 12 67.97 5.54 1.3792 0 5 4 6 68.03 3.83 1.3780 3 3 0 6 69.13 1.45 1.3588 3 1 11 12 69.35 5.76 1.3550 2 0 14 6 69.75 4.61 1.3482 4 0 10 6 71.68 3.89 1.3166 2 2 12 12 72.21 4.92 1.3083 2 4 4 12 72.92 3.40 1.2973 1 1 15 12 73.56 5.99 1.2876 1 2 14 12 73.83 2.36 1.2835 5 1 1 12 73.95 2.68 1.2818 3 2 10 12 76.35 9.25 1.2474 5 1 4 12 77.84 1.46 1.2271 1 5 5 12 80.23 1.89 1.1965 4 2 8 12 80.48 6.93 1.1934 6 0 0 6 81.72 3.26 1.1783 3 1 14 12 81.80 2.12 1.1775 5 1 7 12 85.24 3.34 1.1386 0 0 18 2 86.11 1.68 1.1292 2 4 10 12 89.23 1.70 1.0977 1 1 18 12 89.72 4.81 1.0929 2 3 14 12 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.