Er O6 Ru Sr2 Battle P, Jones C, Studer F Journal of Solid State Chemistry 90 (1991) 302-312 The crystal and magnetic structures of Ca2NdRuO6,Ca2HoRuO6 and Sr2ErRuO6 _cod_database_code 1001472 _database_code_amcsd 0013698 CELL PARAMETERS: 5.7626 5.7681 8.1489 90.000 90.190 90.000 SPACE GROUP: P2_1/n X-RAY WAVELENGTH: 1.541838 Cell Volume: 270.862 Density (g/cm3): 6.615 MAX. ABS. INTENSITY / VOLUME**2: 106.7114290 RIR: 5.253 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.83 1.68 4.7124 -1 0 1 2 18.85 5.65 4.7080 0 1 1 4 18.89 3.11 4.6977 1 0 1 2 21.80 23.91 4.0767 1 1 0 4 21.81 11.47 4.0744 0 0 2 2 30.99 100.00 2.8852 -1 1 2 4 31.01 49.58 2.8840 0 2 0 2 31.04 48.81 2.8813 2 0 0 2 31.07 99.45 2.8785 1 1 2 4 36.53 2.58 2.4599 -1 2 1 4 36.53 4.34 2.4597 -2 1 1 4 36.57 1.36 2.4574 0 1 3 4 36.62 2.45 2.4539 1 0 3 2 44.45 52.10 2.0384 2 2 0 4 44.47 26.96 2.0372 0 0 4 2 48.65 1.73 1.8717 -1 2 3 4 48.78 1.51 1.8670 2 1 3 4 49.98 2.14 1.8247 -2 2 2 4 50.00 2.45 1.8241 -1 1 4 4 50.01 3.12 1.8239 1 3 0 4 50.05 1.87 1.8225 3 1 0 4 50.09 2.70 1.8212 2 2 2 4 50.10 1.88 1.8206 1 1 4 4 51.35 1.15 1.7794 1 3 1 4 55.13 9.55 1.6660 -2 0 4 2 55.14 18.12 1.6656 -3 1 2 4 55.15 15.48 1.6653 -1 3 2 4 55.20 16.55 1.6640 1 3 2 4 55.20 17.87 1.6640 0 2 4 4 55.28 19.21 1.6617 3 1 2 4 55.31 8.30 1.6608 2 0 4 2 64.60 12.71 1.4426 -2 2 4 4 64.63 6.10 1.4420 0 4 0 2 64.70 6.17 1.4406 4 0 0 2 64.77 12.73 1.4392 2 2 4 4 73.40 5.77 1.2900 -3 3 2 4 73.43 5.55 1.2895 2 4 0 4 73.44 6.18 1.2894 -1 1 6 4 73.48 5.68 1.2888 4 2 0 4 73.52 5.68 1.2882 3 3 2 4 73.56 6.23 1.2876 1 1 6 4 81.75 2.56 1.1781 -4 0 4 2 81.84 4.99 1.1770 0 4 4 4 82.06 2.58 1.1744 4 0 4 2 89.96 3.27 1.0907 -3 1 6 4 89.96 3.43 1.0906 -4 2 4 4 89.99 3.25 1.0903 -2 4 4 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.