Cr2 F5 Lacorre P, Ferey G, Pannetier J Journal of Solid State Chemistry 96 (1992) 227-236 The magnetic structure of Cr2 F5 _cod_database_code 1000420 _database_code_amcsd 0013723 CELL PARAMETERS: 7.7526 7.5228 7.4477 90.000 124.081 90.000 SPACE GROUP: C2/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 359.756 Density (g/cm3): 3.673 MAX. ABS. INTENSITY / VOLUME**2: 23.67218840 RIR: 2.098 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.16 2.00 4.8839 1 1 0 4 23.65 100.00 3.7614 0 2 0 2 26.59 71.17 3.3528 -2 0 2 2 26.81 3.65 3.3249 -1 1 2 4 27.79 77.12 3.2105 2 0 0 2 28.95 39.37 3.0843 0 0 2 2 33.21 1.45 2.6979 -2 2 1 4 35.88 17.76 2.5028 -2 2 2 4 36.81 11.75 2.4420 2 2 0 4 37.21 11.29 2.4161 -3 1 2 4 37.72 4.48 2.3850 0 2 2 4 37.89 1.79 2.3745 -3 1 1 4 38.32 5.66 2.3487 -1 3 1 4 39.65 4.56 2.2729 -1 1 3 4 40.72 4.39 2.2160 1 1 2 4 42.18 3.14 2.1426 -3 1 3 4 43.98 4.92 2.0587 3 1 0 4 46.93 14.49 1.9359 -4 0 2 2 48.40 25.64 1.8807 0 4 0 2 49.16 21.72 1.8533 -2 0 4 2 51.07 2.51 1.7884 -3 3 2 4 51.30 16.55 1.7808 2 0 2 2 51.44 1.25 1.7764 -3 1 4 4 53.21 9.76 1.7213 -4 2 2 4 53.85 1.10 1.7025 1 3 2 4 54.76 4.71 1.6764 -4 0 4 2 55.26 17.61 1.6625 -2 2 4 4 56.07 16.41 1.6403 -2 4 2 4 56.73 13.24 1.6228 2 4 0 4 57.24 7.32 1.6096 2 2 2 4 57.38 12.10 1.6057 0 4 2 4 57.40 12.20 1.6053 4 0 0 2 59.99 7.06 1.5421 0 0 4 2 60.46 5.07 1.5312 -4 2 4 4 61.21 1.10 1.5142 -5 1 3 4 62.95 6.93 1.4764 4 2 0 4 65.41 4.33 1.4269 0 2 4 4 69.71 7.78 1.3490 -4 4 2 4 71.47 8.31 1.3201 -2 4 4 4 73.19 9.23 1.2931 2 4 2 4 74.58 1.12 1.2724 -1 5 3 4 75.88 1.32 1.2538 0 6 0 2 76.06 2.54 1.2514 -4 4 4 4 78.31 6.15 1.2210 4 4 0 4 80.55 4.02 1.1925 0 4 4 4 81.68 1.08 1.1789 4 0 2 2 82.06 2.11 1.1744 -2 6 2 4 83.17 1.34 1.1615 0 6 2 4 83.35 2.28 1.1594 2 0 4 2 88.18 1.48 1.1080 2 2 4 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.