Ba2 Ca Cu2 O8 Tl1.81 Michel C, Martin C, Hervieu M, Maignan A, Provost J, Huve M, Raveau B Journal of Solid State Chemistry 96 (1992) 271-286 Thallium nonstoichiometry in 2212-thallium cuprate _cod_database_code 1001533 _database_code_amcsd 0013725 CELL PARAMETERS: 3.8489 3.8489 29.3153 90.000 90.000 90.000 SPACE GROUP: I4/mmm X-RAY WAVELENGTH: 1.541838 Cell Volume: 434.278 Density (g/cm3): 7.186 MAX. ABS. INTENSITY / VOLUME**2: 167.0524101 RIR: 7.570 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 6.03 35.12 14.6576 0 0 2 2 12.08 1.39 7.3288 0 0 4 2 18.16 3.89 4.8859 0 0 6 2 24.86 1.24 3.5811 1 0 3 8 27.73 68.31 3.2175 1 0 5 8 30.49 1.39 2.9315 0 0 10 2 31.57 100.00 2.8339 1 0 7 8 32.91 82.47 2.7216 1 1 0 4 33.49 12.91 2.6758 1 1 2 8 36.13 4.31 2.4864 1 0 9 8 36.79 21.12 2.4429 0 0 12 2 41.20 7.67 2.1911 1 0 11 8 41.32 2.72 2.1849 1 1 8 8 43.20 4.22 2.0940 0 0 14 2 45.48 6.89 1.9945 1 1 10 8 46.68 3.38 1.9457 1 0 13 8 47.23 36.62 1.9245 2 0 0 4 47.66 1.45 1.9081 2 0 2 8 50.18 23.71 1.8180 1 1 12 8 55.36 8.50 1.6596 1 1 14 8 55.65 17.98 1.6516 2 1 5 16 56.50 3.34 1.6286 0 0 18 2 57.27 1.09 1.6088 2 0 10 8 57.92 32.04 1.5921 2 1 7 16 58.66 7.73 1.5737 1 0 17 8 60.87 1.03 1.5219 2 1 9 16 61.32 15.69 1.5117 2 0 12 8 64.44 3.61 1.4459 2 1 11 16 65.14 7.05 1.4321 1 0 19 8 65.92 4.11 1.4169 2 0 14 8 66.96 5.04 1.3975 1 1 18 8 68.59 1.76 1.3682 2 1 13 16 69.02 9.57 1.3608 2 2 0 4 75.92 3.23 1.2533 3 0 5 8 76.65 4.51 1.2432 2 0 18 8 77.87 5.98 1.2267 3 0 7 8 78.52 5.70 1.2182 2 1 17 16 78.60 9.80 1.2171 3 1 0 8 78.92 1.55 1.2130 3 1 2 16 80.85 6.07 1.1888 2 2 12 8 84.29 6.20 1.1489 2 1 19 16 85.01 1.82 1.1410 2 2 14 8 86.60 1.60 1.1241 3 1 10 16 86.83 3.44 1.1217 1 0 25 8 87.54 2.40 1.1144 1 1 24 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.