La O3 V Bordet P, Chaillout C, Marezio M, Huang Q, Santoro A, Cheong S, Takagi H, Oglesby C, Batlogg B Journal of Solid State Chemistry 106 (1993) 253-270 Structural aspects of the crystallographic-magnetic transition in LaVO3 around 140 K _cod_database_code 1008645 _database_code_amcsd 0016534 CELL PARAMETERS: 5.5581 7.8342 5.5486 90.000 90.000 90.000 SPACE GROUP: Pnma X-RAY WAVELENGTH: 1.541838 Cell Volume: 241.605 Density (g/cm3): 6.538 MAX. ABS. INTENSITY / VOLUME**2: 153.0295881 RIR: 7.621 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 22.64 18.94 3.9268 1 0 1 4 22.70 10.48 3.9171 0 2 0 2 25.37 4.73 3.5105 1 1 1 8 32.21 23.60 2.7791 2 0 0 2 32.27 24.52 2.7743 0 0 2 2 32.28 100.00 2.7732 1 2 1 8 34.24 3.22 2.6191 2 1 0 4 38.03 1.03 2.3663 1 1 2 8 39.77 12.73 2.2666 2 2 0 4 39.82 13.67 2.2640 0 2 2 4 41.53 1.75 2.1745 1 3 1 8 46.24 26.43 1.9634 2 0 2 4 46.36 14.15 1.9586 0 4 0 2 47.76 3.07 1.9045 2 1 2 8 47.79 1.84 1.9030 2 3 0 4 52.11 2.80 1.7553 2 2 2 8 52.12 2.11 1.7549 1 0 3 4 52.19 3.61 1.7526 1 4 1 8 53.43 4.65 1.7147 3 1 1 8 57.48 13.06 1.6034 3 2 1 8 57.55 18.61 1.6015 1 2 3 8 57.57 8.50 1.6009 2 4 0 4 57.61 8.96 1.6000 0 4 2 4 63.84 2.19 1.4579 3 3 1 8 67.39 2.40 1.3895 4 0 0 2 67.53 3.10 1.3872 0 0 4 2 67.56 11.86 1.3866 2 4 2 8 68.59 1.40 1.3682 4 1 0 4 72.29 1.43 1.3070 1 4 3 8 73.33 1.25 1.2910 3 1 3 8 76.71 1.86 1.2424 4 0 2 4 76.78 4.52 1.2415 3 2 3 8 76.80 2.39 1.2411 2 0 4 4 76.96 5.76 1.2390 1 6 1 8 77.84 1.53 1.2271 4 1 2 8 81.32 1.14 1.1832 2 2 4 8 82.42 1.11 1.1702 3 3 3 8 82.48 1.07 1.1695 3 5 1 8 85.73 1.89 1.1333 4 4 0 4 85.85 2.52 1.1320 0 4 4 4 86.81 1.50 1.1219 4 3 2 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.