Wakefieldite-(Ce) Chakoumakos B C, Abraham M M, Boatner L A Journal of Solid State Chemistry 109 (1994) 197-202 Crystal structure refinements of zircon-type MVO4 (M = Sc, Y, Ce, Pr, Nd, Tb, Ho, Er, Tm, Yb, Lu) Locality: synthetic _database_code_amcsd 0013801 CELL PARAMETERS: 7.4004 7.4004 6.4972 90.000 90.000 90.000 SPACE GROUP: I4_1/amd X-RAY WAVELENGTH: 1.541838 Cell Volume: 355.825 Density (g/cm3): 4.760 MAX. ABS. INTENSITY / VOLUME**2: 120.8539196 RIR: 8.266 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.17 27.75 4.8825 1 0 1 8 24.05 100.00 3.7002 2 0 0 4 30.31 8.89 2.9490 2 1 1 16 32.44 66.83 2.7600 1 1 2 8 34.27 20.77 2.6164 2 2 0 4 36.82 3.20 2.4412 2 0 2 8 39.06 13.43 2.3062 3 0 1 8 43.54 8.49 2.0786 1 0 3 8 46.39 11.70 1.9572 3 2 1 16 47.91 54.91 1.8988 3 1 2 16 49.25 14.42 1.8501 4 0 0 4 50.35 4.29 1.8122 2 1 3 16 52.92 2.65 1.7301 4 1 1 16 55.53 12.06 1.6548 4 2 0 8 56.55 1.84 1.6275 3 0 3 8 56.67 2.77 1.6243 0 0 4 2 60.22 15.70 1.5368 3 3 2 8 62.44 10.22 1.4873 2 0 4 8 64.58 4.20 1.4431 4 3 1 16 67.81 2.25 1.3820 4 1 3 16 67.92 9.44 1.3800 2 2 4 8 71.15 12.02 1.3251 5 1 2 16 72.21 2.99 1.3082 4 4 0 4 77.37 4.16 1.2334 6 0 0 4 78.23 1.39 1.2220 5 0 3 8 78.33 4.89 1.2206 4 0 4 8 79.19 2.04 1.2095 2 1 5 16 80.28 1.17 1.1958 6 1 1 16 81.41 9.84 1.1821 5 3 2 16 82.42 4.97 1.1701 6 2 0 8 83.27 1.27 1.1603 5 2 3 16 83.37 9.86 1.1592 4 2 4 16 89.20 1.33 1.0979 3 2 5 16 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.