Ba2.5 Co2 Cu3 Eu2.5 O12 Barbey L, Domenges B, Nguyen N, Raveau B Journal of Solid State Chemistry 111 (1994) 238-246 Eu2.5Ba2.5Co2Cu3O12, an intergrowth of the "112" and "123" structures _cod_database_code 1001601 _database_code_amcsd 0013812 CELL PARAMETERS: 3.8935 3.8935 19.0850 90.000 90.000 90.000 SPACE GROUP: P4/mmm X-RAY WAVELENGTH: 1.541838 Cell Volume: 289.316 Density (g/cm3): 7.023 MAX. ABS. INTENSITY / VOLUME**2: 221.9652551 RIR: 10.292 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 4.63 1.50 19.0850 0 0 1 2 9.27 5.57 9.5425 0 0 2 2 22.84 13.40 3.8935 1 0 0 4 23.30 5.23 3.8170 0 0 5 2 24.70 1.13 3.6050 1 0 2 8 32.52 48.33 2.7531 1 1 0 4 32.86 100.00 2.7257 1 0 5 8 37.71 1.27 2.3856 0 0 8 2 40.39 3.94 2.2333 1 0 7 8 40.39 15.34 2.2329 1 1 5 8 46.66 27.33 1.9468 2 0 0 4 47.65 9.03 1.9085 0 0 10 2 52.56 2.41 1.7412 2 1 0 8 52.79 2.02 1.7342 2 0 5 8 53.47 1.87 1.7137 1 0 10 8 58.24 32.34 1.5842 2 1 5 16 58.88 15.05 1.5685 1 1 10 8 63.38 1.63 1.4675 2 1 7 16 68.12 6.88 1.3766 2 2 0 4 68.90 9.57 1.3628 2 0 10 8 73.64 1.21 1.2863 2 1 10 16 77.53 5.68 1.2312 3 1 0 8 77.72 5.82 1.2287 3 0 5 8 79.20 3.82 1.2094 1 0 15 8 82.28 2.20 1.1718 3 1 5 16 87.34 4.30 1.1164 2 2 10 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.