Ba Co1.2 Cu0.8 O5 Y Barbey L, Nguyen N, Caignaert V, Studer F, Raveau B Journal of Solid State Chemistry 112 (1994) 148-156 Spin state and variation of the spin orientation of Co(III) in the 112- type phase YBa(Co2-xCux)O5 _cod_database_code 1001608 _database_code_amcsd 0013826 CELL PARAMETERS: 3.8675 3.8675 7.5238 90.000 90.000 90.000 SPACE GROUP: P4/mmm X-RAY WAVELENGTH: 1.541838 Cell Volume: 112.538 Density (g/cm3): 6.311 MAX. ABS. INTENSITY / VOLUME**2: 165.0066426 RIR: 8.513 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 23.00 5.95 3.8675 1 0 0 4 23.65 2.05 3.7619 0 0 2 2 25.90 3.05 3.4397 1 0 1 8 32.75 43.27 2.7347 1 1 0 4 33.22 100.00 2.6966 1 0 2 8 34.91 3.38 2.5702 1 1 1 8 35.80 5.52 2.5079 0 0 3 2 40.79 11.53 2.2120 1 1 2 8 46.99 28.90 1.9338 2 0 0 4 48.39 8.58 1.8809 0 0 4 2 52.94 1.02 1.7296 2 1 0 8 54.23 1.55 1.6915 1 0 4 8 58.76 32.10 1.5715 2 1 2 16 59.66 16.43 1.5498 1 1 4 8 60.45 3.32 1.5314 2 0 3 8 66.70 1.17 1.4024 1 0 5 8 68.64 7.17 1.3674 2 2 0 4 69.75 9.23 1.3483 2 0 4 8 74.53 1.02 1.2732 2 1 4 16 78.15 5.18 1.2230 3 1 0 8 78.42 5.78 1.2195 3 0 2 8 79.90 1.14 1.2005 2 2 3 8 80.53 4.15 1.1928 1 0 6 8 83.03 1.56 1.1631 3 1 2 16 85.54 1.04 1.1353 2 1 5 16 88.38 4.22 1.1060 2 2 4 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.