O4 Ru Sr2 Huang Q, Soubeyroux J, Chmaissem O, Natali Sora I, Santoro A, Cava R, Krajewski J, Peck W Journal of Solid State Chemistry 112 (1994) 355-361 Neutron powder diffraction study of the crystal structures of Sr2RuO4 and Sr2IrO4 at room temperature and at 10K _cod_database_code 1008659 _database_code_amcsd 0016547 CELL PARAMETERS: 3.8730 3.8730 12.7323 90.000 90.000 90.000 SPACE GROUP: I4/mmm X-RAY WAVELENGTH: 1.541838 Cell Volume: 190.986 Density (g/cm3): 5.917 MAX. ABS. INTENSITY / VOLUME**2: 136.4343717 RIR: 7.508 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.91 19.50 6.3661 0 0 2 2 24.02 1.24 3.7054 1 0 1 8 31.27 100.00 2.8608 1 0 3 8 32.70 62.99 2.7386 1 1 0 4 42.49 12.42 2.1278 1 0 5 8 42.60 16.17 2.1221 0 0 6 2 43.60 5.84 2.0760 1 1 4 8 46.92 30.66 1.9365 2 0 0 4 49.18 2.37 1.8527 2 0 2 8 54.72 17.22 1.6774 1 1 6 8 57.47 30.05 1.6037 2 1 3 16 57.94 2.51 1.5915 0 0 8 2 65.13 5.59 1.4322 2 1 5 16 65.22 13.82 1.4304 2 0 6 8 68.15 3.00 1.3760 1 1 8 8 68.53 7.61 1.3693 2 2 0 4 70.92 3.23 1.3288 1 0 9 8 77.24 5.41 1.2351 3 0 3 8 77.66 3.50 1.2296 2 0 8 8 78.02 6.89 1.2248 3 1 0 8 84.06 1.19 1.1515 3 0 5 8 84.14 5.62 1.1506 2 2 6 8 88.08 3.42 1.1090 1 0 11 8 89.43 3.23 1.0957 2 1 9 16 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.