Cu0.36 Nb2 O6 Zn0.64 Norwig J, Weitzel H, Paulus H, Lautenschlaeger G, Rodriguez-Carvajal J, Fuess H Journal of Solid State Chemistry 115 (1995) 476-483 Structural relations in mixed oxides Cux Zn1-x Nb2 O6 _cod_database_code 1006089 _database_code_amcsd 0013853 CELL PARAMETERS: 14.1870 5.7300 5.0310 90.000 90.000 90.000 SPACE GROUP: Pbcn X-RAY WAVELENGTH: 1.541838 Cell Volume: 408.978 Density (g/cm3): 5.627 MAX. ABS. INTENSITY / VOLUME**2: 132.9357358 RIR: 7.692 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 12.48 1.11 7.0935 2 0 0 2 24.37 3.75 3.6531 1 1 1 8 24.41 24.78 3.6473 3 1 0 4 25.11 2.46 3.5468 4 0 0 2 30.27 100.00 2.9529 3 1 1 8 31.22 10.07 2.8650 0 2 0 2 35.69 12.86 2.5155 0 0 2 2 36.08 13.87 2.4896 0 2 1 4 38.06 6.61 2.3645 6 0 0 2 40.62 2.64 2.2209 3 0 2 4 40.97 5.15 2.2030 3 2 1 8 43.71 7.29 2.0708 3 1 2 8 48.14 7.13 1.8903 0 2 2 4 50.01 6.32 1.8236 6 2 0 4 51.14 1.43 1.7862 7 1 1 8 51.61 12.88 1.7710 3 3 0 4 53.16 15.72 1.7229 6 0 2 4 53.44 19.41 1.7145 6 2 1 8 54.97 1.41 1.6705 3 3 1 8 60.79 13.16 1.5237 3 1 3 8 62.95 4.94 1.4765 6 2 2 8 63.99 10.49 1.4549 9 1 1 8 64.33 11.61 1.4481 3 3 2 8 64.37 7.18 1.4473 0 2 3 4 68.05 5.41 1.3777 0 4 1 4 72.69 1.81 1.3009 9 1 2 8 75.60 1.49 1.2578 0 0 4 2 77.29 1.83 1.2344 6 2 3 8 78.71 2.59 1.2158 9 3 0 4 80.72 5.50 1.1904 6 4 1 8 80.84 1.09 1.1890 3 1 4 8 81.40 2.00 1.1823 12 0 0 2 84.04 1.16 1.1517 0 2 4 4 86.40 3.39 1.1262 9 1 3 8 87.61 1.51 1.1138 3 5 0 4 87.94 2.97 1.1104 6 0 4 4 89.54 4.45 1.0946 9 3 2 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.