Cu0.85 Nb2 O6 Zn0.15 Norwig J, Weitzel H, Paulus H, Lautenschlaeger G, Rodriguez-Carvajal J, Fuess H Journal of Solid State Chemistry 115 (1995) 476-483 Structural relations in mixed oxides Cux Zn1-x Nb2 O6 _cod_database_code 1006091 _database_code_amcsd 0013855 CELL PARAMETERS: 5.0070 14.1706 5.7547 90.000 91.451 90.000 SPACE GROUP: P2_1/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 408.178 Density (g/cm3): 5.624 MAX. ABS. INTENSITY / VOLUME**2: 61.92601176 RIR: 3.586 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 12.49 3.05 7.0853 0 2 0 2 24.10 3.56 3.6923 -1 1 1 4 24.38 57.63 3.6506 0 3 1 4 24.68 4.16 3.6068 1 1 1 4 25.14 4.63 3.5426 0 4 0 2 26.48 3.62 3.3654 -1 2 1 4 30.06 100.00 2.9723 -1 3 1 4 30.54 97.91 2.9272 1 3 1 4 31.09 17.47 2.8764 0 0 2 2 31.74 1.16 2.8189 0 1 2 4 35.60 17.75 2.5217 -1 0 2 2 35.88 24.38 2.5027 2 0 0 2 36.18 1.05 2.4827 -1 1 2 4 36.42 13.56 2.4671 1 0 2 2 38.10 13.62 2.3618 0 6 0 2 40.39 1.24 2.2330 0 4 2 4 40.55 4.52 2.2245 -1 3 2 4 40.80 5.06 2.2115 2 3 0 4 41.28 5.16 2.1868 1 3 2 4 43.51 8.01 2.0798 -2 3 1 4 44.08 1.18 2.0544 -1 4 2 4 44.20 7.61 2.0489 2 3 1 4 47.55 5.34 1.9122 -2 0 2 2 48.01 1.04 1.8950 -2 1 2 4 48.31 1.41 1.8839 -1 5 2 4 48.84 5.84 1.8648 2 0 2 2 49.23 1.80 1.8510 0 2 3 4 49.97 10.08 1.8253 0 6 2 4 51.05 1.24 1.7892 -1 7 1 4 51.35 1.22 1.7792 1 7 1 4 51.43 23.27 1.7768 0 3 3 4 53.13 17.67 1.7238 -1 6 2 4 53.34 30.77 1.7177 2 6 0 4 53.73 20.38 1.7060 1 6 2 4 54.40 1.22 1.6864 0 4 3 4 60.65 10.84 1.5268 -3 3 1 4 61.01 1.71 1.5187 0 9 1 4 61.47 11.93 1.5084 3 3 1 4 61.58 1.55 1.5059 -2 2 3 4 62.49 3.44 1.4862 -2 6 2 4 63.50 9.08 1.4651 -2 3 3 4 63.57 4.10 1.4636 2 6 2 4 63.78 5.88 1.4594 -3 0 2 2 63.94 9.21 1.4559 -1 9 1 4 64.15 1.66 1.4517 -3 1 2 4 64.21 9.95 1.4506 1 9 1 4 64.83 1.55 1.4382 0 0 4 2 65.09 10.39 1.4330 2 3 3 4 65.37 6.78 1.4276 3 0 2 2 66.12 1.14 1.4132 -2 4 3 4 67.28 3.31 1.3917 -1 0 4 2 67.64 1.46 1.3850 -1 1 4 4 68.31 4.05 1.3731 1 0 4 2 72.60 1.93 1.3022 -2 9 1 4 73.10 1.78 1.2945 2 9 1 4 76.06 2.60 1.2513 4 0 0 2 76.21 1.05 1.2492 -1 5 4 4 76.77 1.77 1.2415 -3 6 2 4 78.25 1.72 1.2218 3 6 2 4 78.62 4.33 1.2169 0 9 3 4 80.03 3.58 1.1990 -1 6 4 4 80.79 1.03 1.1896 -4 3 1 4 81.00 3.73 1.1871 1 6 4 4 81.51 3.62 1.1809 0 12 0 2 86.34 2.57 1.1268 -3 9 1 4 87.06 2.84 1.1194 3 9 1 4 87.20 1.32 1.1179 0 3 5 4 88.41 4.48 1.1057 4 6 0 4 88.66 1.04 1.1033 -3 0 4 2 88.85 3.28 1.1014 -2 9 3 4 89.32 1.35 1.0968 -1 3 5 4 89.77 1.11 1.0924 0 12 2 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.