Ba Co Cu0.5 Fe0.5 O5 Y Barbey L, Nguyen N, Ducouret A, Caignaert V, Greneche J, Raveau B Journal of Solid State Chemistry 115 (1995) 514-520 Magnetic behaviour of the "112" type substituted cuprate YBaCoCu1-xFexO5 _cod_database_code 1001648 _database_code_amcsd 0013856 CELL PARAMETERS: 3.8785 3.8785 7.5441 90.000 90.000 90.000 SPACE GROUP: P4/mmm X-RAY WAVELENGTH: 1.541838 Cell Volume: 113.484 Density (g/cm3): 6.216 MAX. ABS. INTENSITY / VOLUME**2: 162.5719252 RIR: 8.516 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 22.93 6.59 3.8785 1 0 0 4 23.59 2.08 3.7720 0 0 2 2 25.83 2.24 3.4493 1 0 1 8 32.65 42.48 2.7425 1 1 0 4 33.13 100.00 2.7041 1 0 2 8 34.81 4.04 2.5775 1 1 1 8 35.70 4.51 2.5147 0 0 3 2 40.67 11.84 2.2182 1 1 2 8 46.85 28.61 1.9392 2 0 0 4 48.25 9.01 1.8860 0 0 4 2 52.78 1.15 1.7345 2 1 0 8 54.07 1.35 1.6961 1 0 4 8 58.58 32.12 1.5759 2 1 2 16 59.48 17.14 1.5540 1 1 4 8 60.27 2.66 1.5357 2 0 3 8 68.42 7.10 1.3713 2 2 0 4 69.53 9.71 1.3520 2 0 4 8 77.89 5.09 1.2265 3 1 0 8 78.15 5.78 1.2230 3 0 2 8 80.26 4.73 1.1961 1 0 6 8 82.74 1.61 1.1664 3 1 2 16 88.07 4.43 1.1091 2 2 4 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.