Bi1.77 Ca0.2 Fe2 O10 Sr3.8 Hervieu M, Pelloquin D, Michel C, Caldes M, Raveau B Journal of Solid State Chemistry 118 (1995) 227-240 The ferrites Bi(n+1) Sr2(n+2) Ba(n-1) Fe(n+1) O6(n+4): a series of intergrowths of the 2201 and 0201 structures _cod_database_code 1001693 _database_code_amcsd 0013872 CELL PARAMETERS: 5.4140 5.4140 18.5240 90.000 90.000 90.000 SPACE GROUP: Cm2a X-RAY WAVELENGTH: 1.541838 Cell Volume: 542.964 Density (g/cm3): 6.009 MAX. ABS. INTENSITY / VOLUME**2: 110.7182912 RIR: 6.000 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 4.77 16.34 18.5240 0 0 1 2 9.55 2.65 9.2620 0 0 2 2 14.34 1.42 6.1747 0 0 3 2 19.17 7.85 4.6310 0 0 4 2 23.73 4.96 3.7491 1 1 1 4 24.02 4.25 3.7048 0 0 5 2 25.17 39.33 3.5380 1 1 2 4 27.41 50.09 3.2537 1 1 3 4 28.92 21.64 3.0873 0 0 6 2 30.29 100.00 2.9506 1 1 4 4 33.09 39.09 2.7070 0 2 0 1 33.09 39.97 2.7070 2 0 0 2 33.45 1.74 2.6786 0 2 1 2 33.45 1.66 2.6786 2 0 1 4 33.66 6.17 2.6623 1 1 5 4 33.87 8.27 2.6463 0 0 7 2 34.52 2.09 2.5983 0 2 2 2 34.52 1.29 2.5983 2 0 2 4 38.89 4.04 2.3155 0 0 8 2 41.48 1.16 2.1768 1 1 7 4 43.99 5.25 2.0582 0 0 9 2 44.51 18.01 2.0354 2 0 6 4 44.51 17.53 2.0354 0 2 6 2 45.80 12.92 1.9813 1 1 8 4 47.50 34.03 1.9141 2 2 0 2 48.08 3.47 1.8923 2 0 7 4 48.08 3.32 1.8923 0 2 7 2 50.33 7.30 1.8128 1 1 9 4 51.67 1.78 1.7690 2 2 4 4 51.97 2.92 1.7596 2 0 8 4 51.97 3.27 1.7596 0 2 8 2 53.77 1.43 1.7048 1 3 1 4 53.91 1.39 1.7006 2 2 5 4 54.51 5.24 1.6835 1 3 2 4 54.51 5.02 1.6835 3 1 2 4 55.08 13.90 1.6675 1 1 10 4 55.72 6.21 1.6498 1 3 3 4 55.72 6.98 1.6498 3 1 3 4 56.14 2.02 1.6384 2 0 9 4 56.14 2.01 1.6384 0 2 9 2 56.57 10.14 1.6268 2 2 6 4 57.38 14.32 1.6058 1 3 4 4 57.38 14.84 1.6058 3 1 4 4 59.48 1.04 1.5541 3 1 5 4 59.61 5.12 1.5509 2 2 7 4 59.92 3.61 1.5437 0 0 12 2 63.01 3.74 1.4753 2 2 8 4 66.73 3.71 1.4017 2 2 9 4 68.11 4.10 1.3766 1 3 8 4 68.11 3.59 1.3766 3 1 8 4 69.44 3.73 1.3535 0 4 0 1 69.44 4.18 1.3535 4 0 0 2 70.19 3.06 1.3410 2 0 12 4 70.19 2.99 1.3410 0 2 12 2 71.71 1.98 1.3162 1 3 9 4 71.71 2.15 1.3162 3 1 9 4 75.15 1.40 1.2642 3 3 2 4 75.64 4.34 1.2573 3 1 10 4 75.64 4.05 1.2573 1 3 10 4 76.18 1.85 1.2497 3 3 3 4 76.91 1.46 1.2396 0 4 6 2 76.91 1.72 1.2396 4 0 6 4 77.61 4.83 1.2302 3 3 4 4 79.11 3.96 1.2106 2 4 0 2 79.11 4.32 1.2106 4 2 0 2 79.82 5.27 1.2016 2 2 12 4 80.86 1.00 1.1887 0 2 14 2 81.98 1.93 1.1753 1 1 15 4 86.32 3.12 1.1271 2 4 6 4 86.32 3.44 1.1271 4 2 6 4 87.23 1.61 1.1176 3 3 8 4 88.16 4.80 1.1082 1 1 16 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.