Tenorite Calos N J, Forrester J S, Schaffer G B Journal of Solid State Chemistry 122 (1996) 273-280 A crystallographic contribution to the mechanism of a mechanically induced solid state reaction Note: milling time = 0 min Locality: synthetic _database_code_amcsd 0018813 CELL PARAMETERS: 4.6832 3.4288 5.1297 90.000 99.309 90.000 SPACE GROUP: C2/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 81.287 Density (g/cm3): 6.499 MAX. ABS. INTENSITY / VOLUME**2: 86.11083047 RIR: 4.314 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 32.52 6.50 2.7537 1 1 0 4 35.47 31.57 2.5311 0 0 2 2 35.58 85.99 2.5232 -1 1 1 4 38.70 100.00 2.3267 1 1 1 4 38.98 24.18 2.3108 2 0 0 2 46.32 1.68 1.9600 -1 1 2 4 48.88 28.06 1.8632 -2 0 2 2 51.33 1.07 1.7800 1 1 2 4 53.45 10.81 1.7144 0 2 0 2 58.26 14.49 1.5837 2 0 2 2 61.63 19.33 1.5048 -1 1 3 4 65.79 15.91 1.4194 0 2 2 4 66.36 14.49 1.4086 -3 1 1 4 67.88 9.75 1.3807 1 1 3 4 68.10 13.89 1.3768 2 2 0 4 72.40 7.67 1.3053 3 1 1 4 75.06 5.33 1.2655 0 0 4 2 75.33 6.20 1.2616 -2 2 2 4 80.40 2.14 1.1943 -2 0 4 2 82.62 4.80 1.1679 -3 1 3 4 83.01 4.43 1.1633 2 2 2 4 83.71 3.56 1.1554 4 0 0 2 86.82 1.68 1.1218 -4 0 2 2 89.74 5.65 1.0927 -1 3 1 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.