Tenorite Calos N J, Forrester J S, Schaffer G B Journal of Solid State Chemistry 122 (1996) 273-280 A crystallographic contribution to the mechanism of a mechanically induced solid state reaction Note: milling time = 10 min Locality: synthetic _database_code_amcsd 0018814 CELL PARAMETERS: 4.6776 3.4593 5.1264 90.000 98.965 90.000 SPACE GROUP: C2/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 81.938 Density (g/cm3): 6.447 MAX. ABS. INTENSITY / VOLUME**2: 80.03569771 RIR: 4.042 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 32.33 5.48 2.7692 1 1 0 4 35.45 36.88 2.5319 0 0 2 2 35.46 100.00 2.5312 -1 1 1 4 38.48 97.00 2.3394 1 1 1 4 38.99 28.52 2.3102 2 0 0 2 49.07 25.38 1.8567 -2 0 2 2 52.94 11.94 1.7297 0 2 0 2 58.09 12.98 1.5878 2 0 2 2 61.62 17.79 1.5051 -1 1 3 4 65.34 15.45 1.4282 0 2 2 4 66.38 13.22 1.4083 -3 1 1 4 67.65 11.05 1.3849 1 1 3 4 67.67 13.36 1.3846 2 2 0 4 72.20 8.62 1.3085 3 1 1 4 75.03 4.47 1.2659 0 0 4 2 75.06 6.88 1.2656 -2 2 2 4 80.66 2.61 1.1912 -2 0 4 2 82.46 4.96 1.1697 2 2 2 4 82.83 5.22 1.1654 -3 1 3 4 83.73 2.91 1.1551 4 0 0 2 87.11 2.04 1.1188 -4 0 2 2 88.86 4.62 1.1012 -1 3 1 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.