Tenorite Calos N J, Forrester J S, Schaffer G B Journal of Solid State Chemistry 122 (1996) 273-280 A crystallographic contribution to the mechanism of a mechanically induced solid state reaction Note: milling time = 25 min Locality: synthetic _database_code_amcsd 0018815 CELL PARAMETERS: 4.6839 3.4734 5.1226 90.000 98.730 90.000 SPACE GROUP: C2/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 82.374 Density (g/cm3): 6.413 MAX. ABS. INTENSITY / VOLUME**2: 84.77345339 RIR: 4.304 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 32.22 4.93 2.7784 1 1 0 4 35.41 100.00 2.5351 -1 1 1 4 35.46 35.95 2.5316 0 0 2 2 38.35 88.49 2.3473 1 1 1 4 38.91 28.09 2.3148 2 0 0 2 49.13 23.30 1.8542 -2 0 2 2 52.71 11.63 1.7367 0 2 0 2 57.92 12.18 1.5922 2 0 2 2 61.65 16.57 1.5046 -1 1 3 4 65.14 14.90 1.4321 0 2 2 4 66.29 12.48 1.4101 -3 1 1 4 67.41 12.93 1.3892 2 2 0 4 67.51 11.08 1.3875 1 1 3 4 71.95 8.69 1.3123 3 1 1 4 74.92 6.86 1.2675 -2 2 2 4 75.04 4.20 1.2658 0 0 4 2 80.82 2.63 1.1892 -2 0 4 2 82.12 5.03 1.1736 2 2 2 4 82.90 5.20 1.1646 -3 1 3 4 83.53 2.79 1.1574 4 0 0 2 87.11 2.08 1.1188 -4 0 2 2 88.46 4.42 1.1052 -1 3 1 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.