Tenorite Calos N J, Forrester J S, Schaffer G B Journal of Solid State Chemistry 122 (1996) 273-280 A crystallographic contribution to the mechanism of a mechanically induced solid state reaction Note: milling time = 30 min Locality: synthetic _database_code_amcsd 0018816 CELL PARAMETERS: 4.6797 3.4768 5.1193 90.000 98.644 90.000 SPACE GROUP: C2/c X-RAY WAVELENGTH: 1.541838 Cell Volume: 82.347 Density (g/cm3): 6.415 MAX. ABS. INTENSITY / VOLUME**2: 83.84666007 RIR: 4.256 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 32.21 4.77 2.7795 1 1 0 4 35.41 100.00 2.5347 -1 1 1 4 35.47 36.96 2.5306 0 0 2 2 38.33 92.35 2.3484 1 1 1 4 38.93 28.94 2.3133 2 0 0 2 49.21 23.70 1.8516 -2 0 2 2 52.65 12.30 1.7384 0 2 0 2 57.91 12.54 1.5924 2 0 2 2 61.69 17.33 1.5037 -1 1 3 4 65.10 15.37 1.4329 0 2 2 4 66.34 13.08 1.4090 -3 1 1 4 67.38 13.36 1.3897 2 2 0 4 67.50 11.51 1.3877 1 1 3 4 71.96 9.07 1.3122 3 1 1 4 74.93 7.31 1.2674 -2 2 2 4 75.08 4.38 1.2653 0 0 4 2 80.94 2.79 1.1878 -2 0 4 2 82.07 5.39 1.1742 2 2 2 4 83.02 5.47 1.1633 -3 1 3 4 83.60 2.93 1.1566 4 0 0 2 87.25 2.22 1.1174 -4 0 2 2 88.38 4.76 1.1060 -1 3 1 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.