KIn(OH)PO4 Hriljac J A, Grey C P, Cheetham A K, VerNooy P D, Torardi C C Journal of Solid State Chemistry 123 (1996) 243-248 Synthesis and structure of KIn(OH)PO4: Chains of hydroxide-bridged InO4(OH)2 octahedra _database_code_amcsd 0013888 CELL PARAMETERS: 9.2770 9.3390 11.2450 90.000 90.000 90.000 SPACE GROUP: P2_12_12_1 X-RAY WAVELENGTH: 1.541838 Cell Volume: 974.243 Density (g/cm3): 3.618 MAX. ABS. INTENSITY / VOLUME**2: 40.07181616 RIR: 3.606 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 13.45 25.83 6.5816 1 1 0 4 15.60 100.00 5.6802 1 1 1 4 19.01 1.88 4.6695 0 2 0 2 19.13 3.91 4.6385 2 0 0 2 20.60 23.09 4.3125 0 2 1 4 20.71 20.50 4.2880 2 0 1 4 20.78 8.60 4.2750 1 1 2 4 22.74 5.50 3.9106 1 2 1 4 22.82 4.48 3.8969 2 1 1 4 26.61 6.30 3.3498 1 2 2 4 26.68 18.03 3.3412 2 1 2 4 27.10 1.30 3.2908 2 2 0 4 27.38 37.42 3.2571 1 1 3 4 28.26 4.46 3.1584 2 2 1 4 29.78 3.14 3.0002 0 3 1 4 30.58 4.16 2.9231 0 2 3 4 30.67 4.98 2.9154 2 0 3 4 31.34 22.12 2.8546 1 3 1 4 31.50 26.26 2.8404 3 1 1 4 31.50 64.59 2.8401 2 2 2 4 31.83 22.22 2.8112 0 0 4 2 32.11 4.04 2.7879 1 2 3 4 32.16 3.88 2.7830 2 1 3 4 33.28 1.09 2.6919 0 1 4 4 34.32 10.45 2.6132 1 3 2 4 34.47 8.47 2.6022 3 1 2 4 34.70 1.45 2.5848 2 3 0 4 34.80 1.29 2.5782 3 2 0 4 37.56 2.01 2.3948 0 3 3 4 38.33 2.31 2.3485 2 3 2 4 38.41 3.41 2.3436 3 2 2 4 38.56 1.93 2.3347 0 4 0 2 38.62 1.23 2.3312 1 2 4 4 38.84 6.69 2.3188 1 3 3 4 38.97 6.28 2.3112 3 1 3 4 40.65 1.46 2.2196 1 4 1 4 40.89 1.62 2.2071 4 1 1 4 41.15 7.88 2.1939 3 3 0 4 41.96 1.80 2.1533 3 3 1 4 42.28 4.39 2.1375 2 2 4 4 42.48 4.10 2.1282 1 1 5 4 42.48 2.33 2.1279 2 3 3 4 43.39 1.40 2.0855 2 4 0 4 44.17 6.64 2.0505 2 4 1 4 44.32 3.23 2.0438 3 3 2 4 44.35 4.92 2.0426 4 2 1 4 44.51 2.33 2.0356 1 3 4 4 44.63 2.32 2.0304 3 1 4 4 44.73 3.01 2.0262 0 2 5 4 44.79 2.93 2.0237 2 0 5 4 46.44 1.72 1.9553 2 4 2 4 46.88 2.22 1.9380 1 4 3 4 47.09 2.81 1.9297 4 1 3 4 47.80 2.59 1.9028 2 3 4 4 47.87 2.51 1.9001 3 2 4 4 48.05 2.49 1.8934 3 3 3 4 48.88 2.25 1.8633 3 4 0 4 48.98 1.25 1.8598 4 3 0 4 49.59 2.24 1.8382 3 4 1 4 49.69 1.70 1.8349 4 3 1 4 49.80 1.28 1.8311 1 5 0 4 50.05 4.66 1.8224 2 4 3 4 50.13 3.08 1.8198 5 1 0 4 50.22 5.91 1.8168 4 2 3 4 50.64 2.76 1.8025 1 1 6 4 50.83 1.48 1.7965 5 1 1 4 50.84 6.99 1.7961 0 4 4 4 51.05 5.08 1.7890 4 0 4 4 51.06 5.14 1.7888 1 3 5 4 51.17 6.35 1.7853 3 1 5 4 51.56 2.63 1.7726 0 5 2 4 51.77 1.45 1.7657 4 3 2 4 51.85 2.39 1.7634 1 4 4 4 51.89 1.64 1.7619 5 0 2 4 52.05 3.00 1.7571 4 1 4 4 52.84 1.19 1.7326 2 5 0 4 52.88 1.66 1.7314 5 1 2 4 52.94 1.94 1.7295 3 3 4 4 53.51 2.05 1.7124 2 5 1 4 53.79 1.94 1.7044 5 2 1 4 54.11 1.46 1.6948 3 2 5 4 55.04 1.52 1.6685 3 4 3 4 55.24 1.28 1.6628 5 0 3 4 55.88 3.69 1.6454 4 4 0 4 55.88 1.22 1.6452 1 5 3 4 56.19 1.03 1.6371 5 1 3 4 56.51 10.60 1.6286 2 2 6 4 58.29 2.86 1.5829 3 5 1 4 58.44 1.94 1.5792 4 4 2 4 58.49 2.33 1.5780 5 3 1 4 58.71 1.52 1.5727 2 5 3 4 58.96 1.39 1.5665 5 2 3 4 59.21 5.11 1.5606 1 1 7 4 60.00 1.67 1.5418 0 6 1 4 60.33 2.58 1.5343 1 5 4 4 60.55 2.15 1.5292 2 4 5 4 60.61 4.30 1.5277 5 1 4 4 60.69 1.26 1.5259 4 2 5 4 60.91 1.22 1.5209 1 6 1 4 61.33 1.11 1.5116 6 1 1 4 62.74 2.19 1.4808 1 6 2 4 63.02 1.26 1.4750 2 5 4 4 63.16 1.20 1.4722 6 1 2 4 63.23 1.62 1.4706 3 5 3 4 63.42 1.83 1.4667 5 3 3 4 64.00 1.07 1.4547 4 5 0 4 64.11 1.12 1.4526 5 4 0 4 64.86 1.47 1.4375 0 6 3 4 65.38 1.67 1.4273 2 6 2 4 65.50 1.63 1.4250 3 3 6 4 65.73 1.08 1.4205 1 6 3 4 65.75 1.30 1.4202 6 2 2 4 65.76 1.51 1.4201 4 4 4 4 66.24 1.47 1.4110 1 3 7 4 66.33 1.04 1.4092 3 1 7 4 66.48 1.41 1.4064 5 4 2 4 66.52 3.25 1.4056 0 0 8 2 68.23 1.34 1.3746 1 1 8 4 68.24 1.03 1.3744 6 3 1 4 72.54 1.22 1.3031 3 5 5 4 72.67 1.41 1.3011 6 2 4 4 73.40 1.20 1.2899 7 0 2 4 74.57 1.13 1.2726 2 4 7 4 74.70 1.87 1.2707 4 2 7 4 77.14 1.05 1.2365 4 4 6 4 84.14 1.20 1.1506 1 3 9 4 84.22 1.17 1.1496 3 1 9 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.