La6MgGe2S14 Gitzendanner R, Spencer C, DiSalvo F, Pell M, Ibers J Journal of Solid State Chemistry 131 (1997) 399-404 Synthesis and structure of a new quaternary rare-earth sulfide, La6MgGe2S14, and the related compound La6MgSi2S14 _cod_database_code 1005055 _database_code_amcsd 0013930 CELL PARAMETERS: 10.3670 10.3670 5.8140 90.000 90.000 120.000 SPACE GROUP: P6_3 X-RAY WAVELENGTH: 1.541838 Cell Volume: 541.143 Density (g/cm3): 4.455 MAX. ABS. INTENSITY / VOLUME**2: 66.66782408 RIR: 4.873 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 17.11 1.86 5.1835 1 1 0 6 18.18 14.69 4.8801 1 0 1 6 19.78 35.77 4.4890 2 0 0 6 22.99 32.99 3.8691 1 1 1 6 25.06 100.00 3.5532 2 0 1 6 26.26 8.74 3.3934 1 2 0 6 26.26 12.23 3.3934 2 1 0 6 30.50 3.00 2.9307 1 2 1 6 30.50 4.99 2.9307 2 1 1 6 30.76 19.94 2.9070 0 0 2 1 32.37 6.97 2.7656 1 0 2 6 33.68 19.18 2.6609 3 0 1 6 34.61 32.09 2.5917 2 2 0 6 35.40 15.00 2.5355 1 1 2 6 36.07 13.01 2.4901 1 3 0 6 36.07 23.06 2.4901 3 1 0 6 36.84 29.59 2.4401 2 0 2 6 38.01 1.28 2.3672 2 2 1 6 39.36 31.60 2.2890 1 3 1 6 39.36 1.23 2.2890 3 1 1 6 40.18 6.77 2.2445 4 0 0 6 40.88 4.77 2.2077 1 2 2 6 40.88 21.20 2.2077 2 1 2 6 43.21 7.59 2.0939 4 0 1 6 43.40 1.82 2.0852 3 0 2 6 43.96 4.92 2.0597 2 3 0 6 46.34 4.37 1.9592 1 4 0 6 46.79 3.14 1.9415 2 3 1 6 46.79 5.97 1.9415 3 2 1 6 46.97 12.38 1.9345 2 2 2 6 48.03 2.45 1.8944 1 0 3 6 48.11 10.93 1.8911 1 3 2 6 48.11 7.13 1.8911 3 1 2 6 49.07 17.05 1.8566 4 1 1 6 50.26 2.99 1.8153 1 1 3 6 51.35 11.06 1.7793 2 0 3 6 51.43 3.15 1.7766 4 0 2 6 53.40 7.76 1.7157 5 0 1 6 54.53 1.30 1.6829 1 2 3 6 54.53 3.13 1.6829 2 1 3 6 54.61 1.81 1.6806 2 3 2 6 55.48 9.56 1.6562 3 3 1 6 56.50 1.04 1.6288 4 2 1 6 56.50 5.19 1.6288 2 4 1 6 56.58 2.60 1.6267 3 0 3 6 56.66 1.32 1.6247 1 4 2 6 56.66 1.09 1.6247 4 1 2 6 57.12 4.29 1.6125 1 5 0 6 60.54 9.86 1.5294 1 3 3 6 62.54 3.11 1.4853 3 3 2 6 62.97 1.90 1.4760 3 4 0 6 62.97 1.19 1.4760 4 3 0 6 63.41 2.52 1.4669 4 0 3 6 64.06 3.57 1.4535 0 0 4 1 64.28 1.32 1.4491 6 0 1 6 64.86 4.41 1.4376 5 2 0 6 65.21 5.43 1.4306 3 4 1 6 66.21 1.65 1.4114 2 3 3 6 66.21 1.51 1.4114 3 2 3 6 66.28 2.91 1.4101 5 1 2 6 66.28 6.85 1.4101 1 5 2 6 66.85 1.73 1.3995 1 1 4 6 68.05 5.05 1.3778 4 1 3 6 68.54 1.95 1.3691 6 1 0 6 70.48 2.41 1.3361 2 1 4 6 70.69 2.12 1.3327 1 6 1 6 70.69 4.36 1.3327 6 1 1 6 71.65 2.70 1.3172 5 0 3 6 71.72 1.68 1.3161 3 4 2 6 71.72 1.89 1.3161 4 3 2 6 73.42 3.58 1.2897 3 3 3 6 73.49 4.48 1.2887 5 2 2 6 74.90 1.84 1.2677 2 2 4 6 75.11 1.31 1.2648 4 4 1 6 75.78 5.30 1.2553 3 1 4 6 75.78 1.09 1.2553 1 3 4 6 75.98 2.67 1.2525 7 0 1 6 75.98 2.58 1.2525 3 5 1 6 76.98 1.12 1.2386 6 1 2 6 82.07 1.62 1.1742 3 4 3 6 82.14 1.01 1.1734 3 5 2 6 82.86 1.92 1.1651 1 7 1 6 86.78 1.04 1.1223 8 0 0 6 87.17 2.95 1.1182 6 1 3 6 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.