Bi9 Cl O18 V2 Mentre O, Abraham F Journal of Solid State Chemistry 136 (1998) 34-45 Synthesis, crystal structure, infrared characterization, and electrical properties of the new Bi9 (V(1-x) P(x))2 Cl O18 series (0 <= x <= 1) _cod_database_code 1004152 _database_code_amcsd 0013948 11.671 5.463 14.792 90 93.67 90 P2_1/m atom x y z occ U(1,1) U(2,2) U(3,3) U(1,2) U(1,3) U(2,3) Bi1 .30514 .25 .21706 .0061 .0112 .0096 0 .0004 0 Bi2 .54312 .25 .65271 .0085 .0092 .0064 0 -.0010 0 Bi3 .86075 .25 .66356 .0080 .0216 .0067 0 .0010 0 Bi4 .95414 .25 .15650 .0064 .0238 .0068 0 .0004 0 Bi5 .61437 .25 .20042 .0074 .0250 .0096 0 .0005 0 Bi6 .26125 .25 .47071 .0102 .0163 .0055 0 -.0006 0 Bi7 .26166 .25 .95538 .0075 .0114 .0069 0 .0001 0 Bi8 .96168 .25 .41215 .0078 .0112 .0099 0 .0005 0 Bi9 .55723 .3057 .91299 .5 .0095 .0158 .0221 .0044 .0041 .0083 V1 .1984 .25 .7196 .006 .008 .008 0 -.001 0 V2 .8609 .25 .9070 .006 .032 .006 0 .000 0 Cl1 .5715 .25 .4330 .081 .026 .022 0 .0004 0 O1 .5995 -.003 .0861 O2 .4538 -.001 .2279 O3 .2950 .505 .3599 O4 .1047 .493 .4526 O5 .3613 .25 .0768 O6 .7612 .25 .8196 O7 .1872 .004 .2101 O8 .0466 .25 .2814 O9 .0975 .25 .6333 O10 .3311 .25 .6865 O11 .9880 .151 .8818 .5 O12 .8725 .586 .9136 .5 O13 .8109 .165 .0025 .5