Cu4Sn7S16 Chen X, Wada H, Sato A, Mieno M Journal of Solid State Chemistry 139 (1998) 144-151 Synthesis, electrical conductivity, and crystal structure of Cu4Sn7S16 and structure refinement of Cu2SnS3 _database_code_amcsd 0013951 CELL PARAMETERS: 7.3720 7.3720 36.0100 90.000 90.000 120.000 SPACE GROUP: R-3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 1694.823 Density (g/cm3): 4.697 MAX. ABS. INTENSITY / VOLUME**2: 67.09495474 RIR: 4.651 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 14.09 1.37 6.2863 1 0 1 6 14.72 42.28 6.0173 0 1 2 6 14.76 40.15 6.0017 0 0 6 2 18.57 4.50 4.7775 0 1 5 6 22.22 2.87 4.0011 0 0 9 2 24.14 3.71 3.6860 1 1 0 6 24.19 6.82 3.6788 0 1 8 6 28.40 49.45 3.1432 2 0 2 6 28.42 48.61 3.1409 1 1 6 12 28.46 34.17 3.1365 1 0 10 6 29.69 15.87 3.0086 0 2 4 6 29.77 1.44 3.0008 0 0 12 2 30.63 1.91 2.9184 2 0 5 6 33.04 2.59 2.7110 1 1 9 12 34.44 100.00 2.6039 2 0 8 6 37.61 4.47 2.3917 1 2 2 12 37.66 5.39 2.3887 0 2 10 6 37.70 9.18 2.3858 0 1 14 6 38.69 3.09 2.3271 1 1 12 12 42.51 2.65 2.1267 1 2 8 12 45.07 1.60 2.0116 1 1 15 12 45.21 4.55 2.0058 0 3 6 6 45.21 7.83 2.0058 3 0 6 6 45.23 21.03 2.0046 2 1 10 12 45.28 7.56 2.0029 2 0 14 6 45.33 2.98 2.0006 0 0 18 2 49.45 50.02 1.8430 2 2 0 6 49.56 40.81 1.8394 0 2 16 6 50.21 1.32 1.8169 1 0 19 6 51.89 2.83 1.7622 3 1 2 12 51.90 8.65 1.7618 2 2 6 12 51.96 8.21 1.7598 1 2 14 12 52.01 3.54 1.7583 1 1 18 12 54.84 1.26 1.6740 2 2 9 12 55.79 1.04 1.6478 3 1 8 12 58.01 5.52 1.5899 0 4 2 6 58.05 6.81 1.5890 1 3 10 12 58.18 1.47 1.5855 1 0 22 6 58.75 2.22 1.5716 4 0 4 6 58.80 1.75 1.5705 2 2 12 12 58.89 2.49 1.5682 2 0 20 6 61.66 14.76 1.5043 0 4 8 6 61.84 6.20 1.5004 0 0 24 2 63.75 2.16 1.4598 2 3 2 12 63.78 1.21 1.4592 4 0 10 6 63.82 2.91 1.4585 3 1 14 12 63.86 1.28 1.4576 0 3 18 6 63.92 3.68 1.4565 0 2 22 6 69.23 3.42 1.3571 1 4 6 12 69.23 1.97 1.3571 4 1 6 12 69.25 2.64 1.3567 3 2 10 12 69.28 1.97 1.3562 0 4 14 6 69.33 4.32 1.3555 2 2 18 12 69.38 1.13 1.3546 2 1 22 12 69.44 1.11 1.3535 0 1 26 6 72.62 10.78 1.3019 4 0 16 6 74.56 1.17 1.2728 2 3 14 12 74.71 1.13 1.2706 2 0 26 6 79.64 1.22 1.2038 4 2 2 12 79.67 1.65 1.2035 0 5 10 6 79.79 1.03 1.2020 1 3 22 12 82.83 3.75 1.1654 4 2 8 12 82.99 13.65 1.1636 2 2 24 12 84.80 1.01 1.1433 4 1 18 12 84.85 1.44 1.1427 4 0 22 6 84.98 1.03 1.1413 1 1 30 12 89.87 1.04 1.0915 3 2 22 12 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.