Bi0.775 O1.5 Pr0.225 Drache M, Obbade S, Wignacourt J, Conflant P Journal of Solid State Chemistry 142 (1999) 349-359 Structural and conductivity properties of Bi(0.775) Ln(0.225) O1.5 oxide conductors (Ln = La, Pr, Nd, Sm, Eu, Gd, Tb, Dy) with rhombohedral Bi-Sr-O type _cod_database_code 1004136 _database_code_amcsd 0013960 CELL PARAMETERS: 3.9975 3.9975 27.5090 90.000 90.000 120.000 SPACE GROUP: R-3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 380.699 Density (g/cm3): 8.543 MAX. ABS. INTENSITY / VOLUME**2: 298.9777329 RIR: 11.395 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 19.36 3.36 4.5848 0 0 6 2 25.94 28.94 3.4348 1 0 1 6 26.55 29.33 3.3572 0 1 2 6 28.87 100.00 3.0922 1 0 4 6 29.22 49.40 3.0566 0 0 9 2 30.51 58.53 2.9301 0 1 5 6 34.53 9.24 2.5977 1 0 7 6 36.84 12.13 2.4397 0 1 8 6 41.95 7.10 2.1537 1 0 10 6 44.70 6.01 2.0272 0 1 11 6 45.37 47.74 1.9987 1 1 0 6 49.76 1.45 1.8322 1 1 6 12 50.55 24.57 1.8055 1 0 13 6 53.01 3.48 1.7276 0 2 1 6 53.34 3.82 1.7174 2 0 2 6 53.63 11.43 1.7089 0 1 14 6 54.68 14.56 1.6786 0 2 4 6 54.88 42.97 1.6728 1 1 9 12 55.67 9.79 1.6512 2 0 5 6 58.24 1.92 1.5841 0 2 7 6 59.82 2.67 1.5461 2 0 8 6 60.08 1.62 1.5399 1 0 16 6 60.59 4.27 1.5283 0 0 18 2 63.46 3.64 1.4659 0 1 17 6 63.50 1.63 1.4651 0 2 10 6 65.59 1.74 1.4233 2 0 11 6 69.57 1.47 1.3513 1 1 15 12 70.25 7.67 1.3398 0 2 13 6 72.29 2.33 1.3070 2 1 1 12 72.57 2.63 1.3026 1 2 2 12 72.82 3.92 1.2989 2 0 14 6 73.70 10.24 1.2854 2 1 4 12 74.54 7.23 1.2730 1 2 5 12 76.77 1.52 1.2415 2 1 7 12 78.16 2.15 1.2229 1 2 8 12 78.84 10.32 1.2141 1 1 18 12 81.41 1.55 1.1821 2 0 17 6 81.45 1.32 1.1816 2 1 10 12 81.92 4.57 1.1760 1 0 22 6 83.36 1.58 1.1594 1 2 11 12 83.83 5.62 1.1540 3 0 0 6 85.99 2.22 1.1305 0 1 23 6 87.69 7.42 1.1129 2 1 13 12 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.