Bi0.775 O1.5 Tb0.225 Drache M, Obbade S, Wignacourt J, Conflant P Journal of Solid State Chemistry 142 (1999) 349-359 Structural and conductivity properties of Bi(0.775) Ln(0.225) O1.5 oxide conductors (Ln = La, Pr, Nd, Sm, Eu, Gd, Tb, Dy) with rhombohedral Bi-Sr-O type _cod_database_code 1004141 _database_code_amcsd 0013965 CELL PARAMETERS: 3.9653 3.9653 27.3170 90.000 90.000 120.000 SPACE GROUP: R-3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 371.977 Density (g/cm3): 8.907 MAX. ABS. INTENSITY / VOLUME**2: 334.5724908 RIR: 12.231 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 19.50 2.96 4.5528 0 0 6 2 26.15 28.51 3.4072 1 0 1 6 26.77 23.79 3.3304 0 1 2 6 29.11 100.00 3.0680 1 0 4 6 29.43 45.64 3.0352 0 0 9 2 30.75 55.50 2.9074 0 1 5 6 34.80 7.41 2.5780 1 0 7 6 37.13 12.90 2.4213 0 1 8 6 42.28 5.58 2.1378 1 0 10 6 45.05 5.07 2.0123 0 1 11 6 45.76 45.25 1.9827 1 1 0 6 50.19 1.22 1.8178 1 1 6 12 50.95 25.88 1.7924 1 0 13 6 53.47 3.45 1.7136 0 2 1 6 53.81 3.06 1.7036 2 0 2 6 54.06 10.37 1.6965 0 1 14 6 55.16 14.46 1.6652 0 2 4 6 55.35 39.68 1.6599 1 1 9 12 56.15 9.23 1.6380 2 0 5 6 58.75 1.50 1.5716 0 2 7 6 60.34 2.86 1.5340 2 0 8 6 61.06 3.74 1.5176 0 0 18 2 63.97 4.19 1.4554 0 1 17 6 64.05 1.28 1.4537 0 2 10 6 66.17 1.46 1.4123 2 0 11 6 70.17 1.29 1.3412 1 1 15 12 70.88 7.99 1.3296 0 2 13 6 72.97 2.30 1.2965 2 1 1 12 73.26 2.11 1.2921 1 2 2 12 73.46 3.51 1.2890 2 0 14 6 74.40 10.11 1.2751 2 1 4 12 75.25 6.78 1.2628 1 2 5 12 77.50 1.19 1.2316 2 1 7 12 78.90 2.31 1.2133 1 2 8 12 79.54 9.05 1.2051 1 1 18 12 82.16 1.79 1.1732 2 0 17 6 82.23 1.04 1.1723 2 1 10 12 82.63 4.72 1.1677 1 0 22 6 84.16 1.34 1.1503 1 2 11 12 84.67 5.31 1.1447 3 0 0 6 86.76 1.82 1.1225 0 1 23 6 88.55 7.72 1.1043 2 1 13 12 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.