Ba6Fe45Ti17O106 Vanderah T A, Wong-Ng W, Toby B H, Browning V M, Shull R D, Geyer R G, Roth R S Journal of Solid State Chemistry 143 (1999) 182-197 Characterization of ternary compounds in the BaO:Fe2O3:TiO2 system: Ba6Fe45Ti17O106 and BaFe11Ti3O23 Note: data from neutron and synchrotron radiation on powder _database_code_amcsd 0013967 19.4119 20.2777 10.0831 90 105.2734 90 C2/m atom x y z occ Biso Ba1 .5 .2149 .0 .4 Ba2 .2388 .0 .1254 .4 Ba3 .5 .3592 -.5 .4 FeM1 .4304 .3460 -.2107 .58 .39 TiM1 .4304 .3460 -.2107 .42 .39 FeM2 .4346 .0785 -.1981 .83 .39 TiM2 .4346 .0785 -.1981 .17 .39 FeM3 .5686 .5 -.3250 .38 .39 TiM3 .5686 .5 -.3250 .62 .39 Fe4 .2785 .0 -.2007 .39 FeM5 .3220 .1374 .0059 .58 .39 TiM5 .3220 .1374 .0059 .42 .39 FeM6 .3228 .2823 -.5131 .84 .39 TiM6 .3228 .2823 -.5131 .16 .39 FeM7 .4293 .0 .0514 .77 .39 TiM7 .4293 .0 .0514 .23 .39 Fe8 .2804 .1473 .3109 .39 FeM9 .3179 .2057 -.2631 .90 .39 TiM9 .3179 .2057 -.2631 .10 .39 FeM10 .3174 .2888 -.0190 .94 .39 TiM10 .3174 .2888 -.0190 .06 .39 FeM11 .5656 .0710 -.3061 .53 .39 TiM11 .5656 .0710 -.3061 .47 .39 FeM12 .3123 .4266 -.4957 .80 .39 TiM12 .3123 .4266 -.4957 .20 .39 FeM13 .4309 .1485 -.4455 .55 .39 TiM13 .4309 .1485 -.4455 .45 .39 FeM14 .4295 .5 -.2217 .40 .39 TiM14 .4295 .5 -.2217 .60 .39 FeM15 .5692 .4224 -.0563 .60 .39 TiM15 .5692 .4224 -.0563 .40 .39 FeM16 .3201 .3659 .2358 .77 .39 TiM16 .3201 .3659 .2358 .23 .39 FeM17 .3313 .0 -.4995 .40 .39 TiM17 .3313 .0 -.4995 .60 .39 FeM18 .4356 .2272 .2854 .53 .39 TiM18 .4356 .2272 .2854 .47 .39 O1 .378 .1453 -.139 .53 O2 .5 .5 .0 .53 O3 .613 .5 -.113 .53 O4 .380 .0 -.148 .53 O5 .255 .0717 -.614 .53 O6 .373 .2833 -.152 .53 O7 .3795 .2152 .104 .53 O8 .502 .288 .246 .53 O9 .628 .3569 -.101 .53 O10 .371 .2098 -.396 .53 O11 .494 .1453 -.261 .53 O12 .505 .0 -.242 .53 O13 .5 .065 .0 .53 O14 .381 .074 -.395 .53 O15 .241 .0 -.403 .53 O16 .377 .0 .349 .53 O17 .257 .1441 .124 .53 O18 .249 .2235 -.617 .53 O19 .371 .3554 -.400 .53 O20 .376 .0699 .105 .53 O21 .502 .430 -.231 .53 O22 .367 .5 -.392 .53 O23 .237 .1473 -.362 .53 O24 .382 .1517 .355 .53 O25 .374 .2909 .341 .53 O26 .258 .2089 -.111 .53 O27 .5 .079 -.5 .53 O28 .387 .4284 -.138 .53 O29 .5 .217 .5 .53 O30 .5 .364 .0 .53 O31 .5 .5 -.5 .53 O32 .252 .0749 -.120 .53 O33 .126 .0707 -.358 .53