La2.25 Li2 Nb1.25 O13 Ti2.75 Crosnier-Lopez M, Bhuvanesh N, Duroy H, Fourquet J Journal of Solid State Chemistry 145 (1999) 136-149 Irreversible electron-induced structural change during HREM imaging in lithium Ruddlesden-Popper phases in the series Li2 La(x) (Nb(2n-3x) Ti(3x-n) O(3n-1)) (n = 2,3,4) and Li2 Sr1.5 (Nb(3-x) Fe(x)) O(10-x) _cod_database_code 1000503 _database_code_amcsd 0013974 CELL PARAMETERS: 3.8800 3.8800 32.4000 90.000 90.000 90.000 SPACE GROUP: I4/mmm X-RAY WAVELENGTH: 1.541838 Cell Volume: 487.762 Density (g/cm3): 5.325 MAX. ABS. INTENSITY / VOLUME**2: 54.00367905 RIR: 3.302 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 5.46 65.86 16.2000 0 0 2 2 10.92 4.09 8.1000 0 0 4 2 16.42 4.68 5.4000 0 0 6 2 23.09 1.18 3.8525 1 0 1 8 24.38 1.42 3.6515 1 0 3 8 26.78 18.77 3.3289 1 0 5 8 27.53 1.61 3.2400 0 0 10 2 30.05 100.00 2.9735 1 0 7 8 32.64 74.80 2.7436 1 1 0 4 33.12 6.20 2.7051 1 1 2 8 33.18 3.04 2.7000 0 0 12 2 33.97 74.98 2.6390 1 0 9 8 34.52 3.85 2.5986 1 1 4 8 36.74 2.79 2.4460 1 1 6 8 39.68 20.84 2.2714 1 1 8 8 43.21 3.93 2.0938 1 1 10 8 44.75 31.85 2.0250 0 0 16 2 46.83 59.30 1.9400 2 0 0 4 47.18 1.50 1.9262 2 0 2 8 47.23 2.73 1.9244 1 1 12 8 50.72 1.28 1.8000 0 0 18 2 54.77 4.17 1.6761 2 1 5 16 56.48 24.38 1.6293 1 1 16 8 56.65 27.51 1.6248 2 1 7 16 58.59 1.86 1.5755 2 0 12 8 59.10 25.84 1.5631 2 1 9 16 61.63 2.45 1.5050 1 1 18 8 65.06 3.22 1.4337 1 0 21 8 66.78 28.96 1.4009 2 0 16 8 68.39 14.39 1.3718 2 2 0 4 71.21 4.74 1.3241 1 0 23 8 71.50 1.46 1.3195 2 0 18 8 76.47 4.80 1.2456 3 0 7 8 77.68 4.93 1.2292 1 0 25 8 77.85 8.67 1.2270 3 1 0 8 78.60 4.86 1.2172 3 0 9 8 79.05 1.12 1.2113 1 1 24 8 82.07 2.07 1.1743 3 1 8 16 83.92 2.70 1.1530 2 1 21 16 85.50 12.10 1.1357 2 2 16 8 89.64 4.57 1.0937 2 1 23 16 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.