Marokite
      Ling C D, Neumeier J J, Argyriou D N
      Journal of Solid State Chemistry 160 (2001) 167-173
      Observation of antiferromagnetism in marokite CaMn2O4
      Locality: synthetic
      Sample: T = 20 K
      _database_code_amcsd 0014006

      CELL PARAMETERS:    3.1469   9.9528   9.6717   90.000   90.000   90.000
      SPACE GROUP: Pbcm      
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:    302.916
      Density (g/cm3):      4.691
      MAX. ABS. INTENSITY / VOLUME**2:      28.27905697    
      RIR:      1.963
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                17.82          1.35        4.9764    0   2   0         2
                18.35         21.60        4.8358    0   0   2         2
                20.07          2.96        4.4250    0   2   1         4
                25.69          7.92        3.4681    0   2   2         4
                28.36          1.45        3.1469    1   0   0         2
                29.78         21.49        3.0004    1   1   0         4
                31.21         28.85        2.8657    1   1   1         8
                33.11        100.00        2.7057    0   2   3         4
                33.70          5.24        2.6597    1   2   0         4
                33.99          2.30        2.6376    1   0   2         4
                34.99         10.36        2.5645    1   2   1         8
                35.20         31.38        2.5496    1   1   2         8
                36.10         25.67        2.4882    0   4   0         2
                37.19          1.74        2.4179    0   0   4         2
                38.63          2.54        2.3305    1   2   2         8
                39.47         37.57        2.2831    1   3   0         4
                40.60         57.55        2.2221    1   3   1         8
                41.10          3.93        2.1964    1   1   3         8
                41.52         15.49        2.1748    0   2   4         4
                43.85         45.35        2.0646    1   3   2         8
                46.53          1.11        1.9518    1   4   0         4
                47.42          2.90        1.9173    1   0   4         4
                48.34          6.67        1.8827    1   1   4         8
                48.88          3.20        1.8632    1   3   3         8
                50.42          6.63        1.8099    1   4   2         8
                50.63          8.22        1.8029    0   2   5         4
                55.34          3.16        1.6600    1   3   4         8
                55.44          4.97        1.6574    1   5   1         8
                56.61         25.93        1.6258    1   1   5         8
                57.14         13.62        1.6119    0   0   6         2
                58.05          8.30        1.5889    1   5   2         8
                58.68         12.35        1.5734    2   0   0         2
                58.86          7.82        1.5691    0   6   2         4
                59.05          4.30        1.5644    1   2   5         8
                59.48          7.62        1.5541    2   1   0         4
                60.64          1.67        1.5271    0   4   5         4
                62.25         25.74        1.4914    1   5   3         8
                62.98         12.95        1.4759    1   3   5         8
                63.02         19.26        1.4750    0   6   3         4
                65.10          1.68        1.4329    2   2   2         8
                65.68          2.11        1.4216    2   3   0         4
                65.76          4.01        1.4200    1   1   6         8
                66.83          2.66        1.3999    2   1   3         8
                69.05         13.05        1.3602    2   2   3         8
                69.48          9.54        1.3529    0   4   6         4
                70.77          1.49        1.3313    0   2   7         4
                70.86          5.91        1.3298    2   4   0         4
                71.67          4.19        1.3168    1   3   6         8
                72.27          1.23        1.3074    2   1   4         8
                72.69          3.84        1.3008    2   3   3         8
                73.02          2.67        1.2957    1   7   0         4
                73.78          1.31        1.2842    1   7   1         8
                73.92          1.38        1.2822    2   4   2         8
                74.79          4.89        1.2694    1   5   5         8
                76.04          3.34        1.2516    1   7   2         8
                76.58          2.79        1.2441    0   8   0         2
                77.33          2.52        1.2339    0   8   1         4
                79.56          1.93        1.2049    0   8   2         4
                81.13          2.92        1.1855    2   2   5         8
                81.41          2.41        1.1821    1   3   7         8
                83.94          3.41        1.1528    2   5   3         8
                86.42          5.51        1.1260    2   0   6         4
                86.86          4.98        1.1214    1   1   8         8
                87.11          1.72        1.1188    2   1   6         8
                87.88          1.48        1.1110    2   6   2         8
================================================================================
       XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs
  For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.