Bohmite Bokhimi X, Sanchez-Valente J, Pedraza F Journal of Solid State Chemistry 166 (2002) 182-190 Crystallization of sol-gel boehmite via hydrothermal annealing Locality: synthetic Sample: annealed t = 3 days, T = 473 K _database_code_amcsd 0014025 CELL PARAMETERS: 2.8656 12.2260 3.6886 90.000 90.000 90.000 SPACE GROUP: Cmcm X-RAY WAVELENGTH: 1.541838 Cell Volume: 129.229 Density (g/cm3): 3.031 MAX. ABS. INTENSITY / VOLUME**2: 24.27696297 RIR: 2.608 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 14.49 100.00 6.1130 0 2 0 2 28.26 43.33 3.1582 0 2 1 4 38.40 37.85 2.3441 1 3 0 4 45.87 4.44 1.9784 1 3 1 8 48.97 28.63 1.8601 1 5 0 4 49.42 18.58 1.8443 0 0 2 2 51.78 5.22 1.7657 0 2 2 4 55.31 11.56 1.6608 1 5 1 8 60.59 5.08 1.5282 0 8 0 2 64.26 12.63 1.4495 1 3 2 8 65.10 6.44 1.4328 2 0 0 2 67.10 2.09 1.3950 2 2 0 4 67.78 6.61 1.3826 1 7 1 8 72.12 12.90 1.3097 1 5 2 8 72.43 3.99 1.3048 2 2 1 8 79.52 1.46 1.2054 0 2 3 4 81.86 3.41 1.1767 0 8 2 4 83.26 3.61 1.1605 0 10 1 4 85.90 4.69 1.1315 2 0 2 4 87.72 1.74 1.1126 2 2 2 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.