Rasvumite Mitchell R H, Ross K C, Potter E G Journal of Solid State Chemistry 177 (2004) 1867-1872 Crystal structures of CsFe2S3 and RbFe2S3: Synthetic analogs of rasvumite KFe2S3 Locality: synthetic _database_code_amcsd 0014044 CELL PARAMETERS: 9.0415 11.0298 5.4177 90.000 90.000 90.000 SPACE GROUP: Cmcm X-RAY WAVELENGTH: 1.541838 Cell Volume: 540.286 Density (g/cm3): 3.036 MAX. ABS. INTENSITY / VOLUME**2: 25.83136309 RIR: 2.770 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 12.66 100.00 6.9924 1 1 0 4 16.07 79.62 5.5149 0 2 0 2 19.64 2.84 4.5208 2 0 0 2 25.48 19.27 3.4962 2 2 0 4 26.17 39.30 3.4058 1 3 0 4 30.43 86.92 2.9376 2 2 1 8 30.75 15.66 2.9073 3 1 0 4 31.02 10.51 2.8834 1 3 1 8 35.03 5.62 2.5617 3 1 1 8 35.54 18.88 2.5259 1 1 2 8 36.57 3.40 2.4575 0 4 1 4 36.97 26.32 2.4314 0 2 2 4 38.63 18.74 2.3308 3 3 0 4 38.75 3.47 2.3236 2 0 2 4 42.65 3.74 2.1200 1 3 2 8 43.26 11.14 2.0915 4 2 0 4 45.78 36.41 1.9819 3 1 2 8 47.02 37.03 1.9324 0 4 2 4 49.59 4.46 1.8383 0 6 0 2 51.33 22.44 1.7801 3 5 0 4 51.43 2.95 1.7769 2 4 2 8 51.74 13.12 1.7668 3 3 2 8 52.34 16.13 1.7481 4 4 0 4 52.74 20.73 1.7355 4 0 2 4 54.60 10.77 1.6807 1 5 2 8 55.21 1.15 1.6636 4 4 1 8 55.51 5.83 1.6555 4 2 2 8 56.66 4.20 1.6245 2 6 1 8 56.73 1.07 1.6227 5 3 0 4 57.43 10.25 1.6045 2 2 3 8 57.79 1.31 1.5955 1 3 3 8 59.46 3.99 1.5544 5 3 1 8 59.56 1.66 1.5523 1 7 0 4 60.90 4.51 1.5211 0 6 2 4 61.54 3.27 1.5069 6 0 0 2 62.21 3.28 1.4922 1 7 1 8 64.06 1.71 1.4536 6 2 0 4 64.65 3.34 1.4417 2 6 2 8 65.44 1.87 1.4262 4 6 0 4 66.61 2.59 1.4040 6 2 1 8 67.02 2.01 1.3964 3 7 0 4 67.99 3.30 1.3787 0 8 0 2 69.39 6.03 1.3544 0 0 4 2 69.83 1.76 1.3468 1 7 2 8 70.87 1.68 1.3297 1 1 4 8 71.55 1.32 1.3188 2 8 0 4 71.76 2.19 1.3153 0 2 4 4 73.87 4.52 1.2829 7 1 0 4 74.01 4.28 1.2809 6 2 2 8 75.24 1.11 1.2630 2 2 4 8 75.31 2.87 1.2620 4 6 2 8 75.55 2.39 1.2586 1 3 4 8 76.80 4.96 1.2412 3 7 2 8 76.96 1.61 1.2389 2 6 3 8 77.79 1.48 1.2277 3 1 4 8 78.81 1.72 1.2144 1 9 0 4 79.39 1.59 1.2070 5 3 3 8 80.89 3.68 1.1883 6 4 2 8 81.82 1.29 1.1772 1 7 3 8 82.34 3.45 1.1711 3 3 4 8 82.83 1.73 1.1654 6 6 0 4 83.27 2.97 1.1604 5 7 1 8 85.39 2.15 1.1369 4 2 4 8 85.81 1.16 1.1324 6 2 3 8 87.84 3.52 1.1113 7 3 2 8 88.68 1.42 1.1030 0 10 0 2 89.98 1.11 1.0904 0 6 4 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.