Maghemite Jorgensen J E, Mosegaard L, Thomsen L E, Jensen T R, Hanson J C Journal of Solid State Chemistry 180 (2007) 180-185 Formation of gamma-Fe2O3 nanoparticles and vacancy ordering: an in situ X-ray powder diffraction study Locality: Synthetic _database_code_amcsd 0020585 CELL PARAMETERS: 8.4053 8.4053 8.4053 90.000 90.000 90.000 SPACE GROUP: Fd-3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 593.827 Density (g/cm3): 4.763 MAX. ABS. INTENSITY / VOLUME**2: 69.46404197 RIR: 4.749 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.28 7.95 4.8528 1 1 1 8 30.07 26.51 2.9717 2 2 0 12 35.42 100.00 2.5343 3 1 1 24 37.05 6.78 2.4264 2 2 2 8 43.05 22.65 2.1013 4 0 0 6 47.13 1.29 1.9283 3 3 1 24 53.40 8.42 1.7157 4 2 2 24 56.92 20.98 1.6176 5 1 1 24 56.92 6.51 1.6176 3 3 3 8 62.51 38.50 1.4859 4 4 0 12 70.91 2.88 1.3290 6 2 0 24 73.95 7.49 1.2818 5 3 3 24 74.95 3.36 1.2671 6 2 2 24 78.91 2.44 1.2132 4 4 4 8 86.68 2.83 1.1232 6 4 2 48 89.58 4.01 1.0943 5 5 3 24 89.58 7.59 1.0943 7 3 1 48 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.