NiP
      Dera P, Lazarz J D, Lavina B
      Journal of Solid State Chemistry 184 (2011) 1997-2003
      Pressure-induced development of bonding in NiAs type compounds and
      polymorphism of NiP
      Locality: Synthetic
      Note: P = 1.29 GPa
      _database_code_amcsd 0018497

      CELL PARAMETERS:    6.0360   4.8684   6.8788   90.000   90.000   90.000
      SPACE GROUP: Pbca      
      X-RAY WAVELENGTH:     1.541838
      Cell Volume:    202.138
      Density (g/cm3):      5.892
      MAX. ABS. INTENSITY / VOLUME**2:      48.37433333    
      RIR:      2.673
      RIR based on corundum from Acta Crystallographica A38 (1982) 733-739
               2-THETA      INTENSITY    D-SPACING   H   K   L   Multiplicity
                25.91         16.18        3.4394    0   0   2         2
                26.86          6.54        3.3191    1   1   1         8
                29.60         16.37        3.0180    2   0   0         2
                29.90        100.00        2.9883    1   0   2         4
                34.98         12.69        2.5651    2   1   0         4
                35.24         29.69        2.5468    1   1   2         8
                36.93         26.46        2.4342    0   2   0         2
                37.42         45.05        2.4034    2   1   1         8
                39.26          9.31        2.2948    0   2   1         4
                39.73          1.98        2.2685    2   0   2         4
                45.66          2.74        1.9869    0   2   2         4
                48.02         40.87        1.8947    2   2   0         4
                48.22         86.95        1.8873    1   2   2         8
                50.87         42.72        1.7950    3   1   1         8
                52.71         25.69        1.7367    3   0   2         4
                53.27         26.25        1.7197    0   0   4         2
                53.61         31.80        1.7095    2   1   3         8
                55.02          5.76        1.6691    0   2   3         4
                55.36          3.08        1.6596    2   2   2         8
                55.57          5.31        1.6539    1   0   4         4
                56.24          3.00        1.6357    3   1   2         8
                60.60         13.91        1.5280    1   3   1         8
                61.27          3.78        1.5128    3   2   1         8
                62.12          2.05        1.4942    2   0   4         4
                64.52          4.32        1.4442    3   1   3         8
                64.67          1.81        1.4413    4   1   0         4
                65.33          2.86        1.4284    2   1   4         8
                66.09          1.70        1.4137    3   2   2         8
                66.25          6.14        1.4107    4   1   1         8
                66.58          5.01        1.4045    0   2   4         4
                68.60          6.88        1.3680    1   2   4         8
                72.27          1.64        1.3073    3   0   4         4
                73.15          2.54        1.2938    1   3   3         8
                74.52         13.76        1.2734    2   2   4         8
                76.71          4.69        1.2424    3   3   1         8
                78.36          8.77        1.2203    4   1   3         8
                78.60          2.63        1.2171    0   4   0         2
                78.93          1.58        1.2129    2   3   3         8
                81.96          1.67        1.1755    1   4   1         8
                83.74          9.19        1.1551    5   1   1         8
                84.51          2.92        1.1465    0   0   6         2
                85.19          2.47        1.1391    5   0   2         4
                86.15          4.44        1.1288    2   4   0         4
                86.30         10.41        1.1272    1   4   2         8
                86.39          1.43        1.1263    1   0   6         4
                87.59          1.48        1.1139    2   4   1         8
                88.38         10.36        1.1060    3   1   5         8
                88.51          1.39        1.1047    4   1   4         8
                89.26          1.32        1.0973    1   1   6         8
                89.91          8.74        1.0911    4   3   1         8
================================================================================
       XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs
  For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.