Ba2 Cu Hg O4.12 Marezio M, Alexandre E, Bordet P, Capponi J, Chaillout C, Kopnin E, Loureiro S, Radaelli P, Van Tendeloo G Journal of Superconductivity 8 (1995) 507-510 Cation and anion disorder in Hg Ba2 Can-1 Cun O2n+2+d _cod_database_code 1008723 _database_code_amcsd 0016607 CELL PARAMETERS: 3.8732 3.8732 9.4809 90.000 90.000 90.000 SPACE GROUP: P4/mmm X-RAY WAVELENGTH: 1.541838 Cell Volume: 142.229 Density (g/cm3): 7.059 MAX. ABS. INTENSITY / VOLUME**2: 269.1708665 RIR: 12.416 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 18.72 1.09 4.7404 0 0 2 2 24.83 33.29 3.5855 1 0 1 8 28.24 9.74 3.1603 0 0 3 2 29.79 100.00 2.9993 1 0 2 8 32.70 51.97 2.7388 1 1 0 4 34.07 3.31 2.6312 1 1 1 8 36.70 2.21 2.4486 1 0 3 8 37.96 11.02 2.3702 0 0 4 2 43.74 17.42 2.0697 1 1 3 8 44.83 4.38 2.0217 1 0 4 8 46.92 21.45 1.9366 2 0 0 4 50.95 12.54 1.7922 1 1 4 8 53.80 6.78 1.7039 2 1 1 16 53.83 12.96 1.7030 1 0 5 8 55.66 5.39 1.6512 2 0 3 8 56.57 28.31 1.6269 2 1 2 16 58.40 1.67 1.5801 0 0 6 2 61.87 8.45 1.4997 2 0 4 8 63.59 2.50 1.4631 1 0 6 8 66.91 2.26 1.3985 2 1 4 16 68.52 5.54 1.3694 2 2 0 4 68.56 2.71 1.3687 1 1 6 8 74.12 1.11 1.2793 3 0 1 8 74.14 8.24 1.2789 2 1 5 16 75.69 1.94 1.2565 2 2 3 8 76.47 5.00 1.2457 3 0 2 8 78.01 5.88 1.2248 3 1 0 8 78.05 2.39 1.2243 2 0 6 8 78.84 2.85 1.2141 1 1 7 8 81.11 3.25 1.1857 2 2 4 8 82.66 2.08 1.1674 2 1 6 16 84.91 3.70 1.1420 3 1 3 16 85.73 2.89 1.1332 1 0 8 8 87.99 1.58 1.1099 2 0 7 8 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.