Pd2As Balz U, Schubert K Journal of the Less-Common Metals 19 (1969) 300-304 Kristallstruktur von Pd2As(r) und Pd2Sb _database_code_amcsd 0014133 CELL PARAMETERS: 3.2450 16.8440 6.5760 90.000 90.000 90.000 SPACE GROUP: Cmc2_1 X-RAY WAVELENGTH: 1.541838 Cell Volume: 359.436 Density (g/cm3): 10.634 MAX. ABS. INTENSITY / VOLUME**2: 121.6837506 RIR: 3.726 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 10.50 1.75 8.4220 0 2 0 2 21.10 1.59 4.2110 0 4 0 2 25.11 1.97 3.5462 0 4 1 2 27.12 2.90 3.2880 0 0 2 1 28.00 2.39 3.1864 1 1 0 4 29.16 5.04 3.0629 0 2 2 2 31.19 21.48 2.8675 1 1 1 4 31.88 4.84 2.8073 0 6 0 2 34.61 3.52 2.5916 0 4 2 2 34.72 57.69 2.5836 1 3 1 4 34.75 10.97 2.5819 0 6 1 2 38.52 38.95 2.3371 1 5 0 4 39.38 42.57 2.2882 1 1 2 4 40.98 100.00 2.2022 1 5 1 4 42.31 96.00 2.1360 1 3 2 4 42.33 29.48 2.1350 0 6 2 2 42.62 48.01 2.1213 0 2 3 2 42.96 24.77 2.1055 0 8 0 2 45.22 32.78 2.0052 0 8 1 2 46.72 32.80 1.9443 0 4 3 2 47.01 1.35 1.9329 1 7 0 4 47.74 13.13 1.9049 1 5 2 4 49.13 10.55 1.8544 1 7 1 4 50.54 13.28 1.8059 1 1 3 4 51.54 1.82 1.7731 0 8 2 2 52.98 2.99 1.7282 1 3 3 4 53.00 5.95 1.7277 0 6 3 2 55.93 1.19 1.6440 0 0 4 1 56.39 4.58 1.6317 0 10 1 2 56.74 32.27 1.6225 2 0 0 2 58.65 3.51 1.5741 1 9 1 4 60.45 4.10 1.5314 0 4 4 2 61.02 2.96 1.5185 0 8 3 2 61.89 4.27 1.4991 0 10 2 2 63.70 3.16 1.4610 1 1 4 4 64.03 1.81 1.4541 1 9 2 4 64.25 3.16 1.4497 1 7 3 4 65.82 7.49 1.4189 1 3 4 4 65.83 1.09 1.4186 0 6 4 2 67.65 2.05 1.3848 1 11 0 4 68.27 2.24 1.3738 2 6 1 4 69.35 5.41 1.3551 1 11 1 4 69.96 2.51 1.3446 1 5 4 4 70.51 3.23 1.3356 0 10 3 2 72.52 9.64 1.3035 1 9 3 4 72.78 1.44 1.2995 0 2 5 2 73.02 1.08 1.2958 0 8 4 2 73.28 8.91 1.2918 2 6 2 4 73.48 14.81 1.2888 2 2 3 4 73.72 8.04 1.2852 2 8 0 4 74.32 11.45 1.2763 1 11 2 4 75.35 11.43 1.2613 2 8 1 4 75.77 2.85 1.2554 0 4 5 2 75.99 3.52 1.2523 1 7 4 4 76.46 12.48 1.2457 2 4 3 4 78.71 10.13 1.2157 1 1 5 4 79.68 2.04 1.2033 1 13 0 4 79.70 1.16 1.2031 0 14 0 2 80.66 1.96 1.1911 1 3 5 4 80.68 1.48 1.1910 0 6 5 2 81.28 10.72 1.1837 1 13 1 4 81.36 2.79 1.1827 2 6 3 4 82.37 1.58 1.1708 1 11 3 4 83.80 10.15 1.1544 1 9 4 4 84.14 2.43 1.1505 2 10 1 4 84.54 2.62 1.1462 1 5 5 4 86.05 3.85 1.1299 0 14 2 2 87.44 1.22 1.1155 0 8 5 2 87.61 2.47 1.1137 2 4 4 4 88.11 1.80 1.1087 2 8 3 4 88.88 2.67 1.1011 2 10 2 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.