Cupalite El-Boragy M, Szepan R, Schubert K Journal of the Less-Common Metals 29 (1972) 133-140 Kristallstruktur von Cu3Al2+ (h) und CuAl (r) Locality: synthetic _database_code_amcsd 0020058 CELL PARAMETERS: 12.0660 4.1050 6.9130 90.000 55.040 90.000 SPACE GROUP: C2/m X-RAY WAVELENGTH: 1.541838 Cell Volume: 280.621 Density (g/cm3): 5.356 MAX. ABS. INTENSITY / VOLUME**2: 54.53524599 RIR: 3.315 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 15.64 12.72 5.6660 2 0 1 2 15.64 14.86 5.6656 0 0 1 2 17.94 1.82 4.9444 2 0 0 2 23.46 41.67 3.7913 1 1 0 4 25.23 19.91 3.5296 1 1 1 4 25.77 17.72 3.4565 2 0 2 2 30.03 21.75 2.9752 -2 0 1 2 31.13 8.32 2.8728 3 1 1 4 31.58 2.93 2.8328 0 0 2 2 35.13 8.70 2.5543 1 1 2 4 40.18 17.93 2.2442 2 0 3 2 43.90 38.49 2.0626 5 1 2 4 44.12 46.30 2.0525 0 2 0 2 44.76 29.03 2.0249 5 1 1 4 44.76 70.97 2.0249 -3 1 1 4 45.09 24.74 2.0109 6 0 2 2 45.09 11.61 2.0107 -2 0 2 2 45.12 69.76 2.0094 3 1 3 4 47.09 1.39 1.9298 2 2 1 4 47.09 1.65 1.9298 0 2 1 4 51.80 4.52 1.7648 2 2 2 4 52.98 1.32 1.7283 4 0 4 2 54.30 7.04 1.6895 -2 2 1 4 56.40 1.69 1.6315 6 0 4 2 58.26 3.00 1.5837 -3 1 2 4 58.71 1.01 1.5726 3 1 4 4 61.19 8.87 1.5146 2 2 3 4 64.92 14.20 1.4364 6 2 2 4 64.92 6.65 1.4363 -2 2 2 4 65.95 2.88 1.4165 8 0 4 2 65.95 9.19 1.4164 0 0 4 2 67.69 3.19 1.3841 8 0 1 2 69.33 1.47 1.3554 1 3 0 4 72.08 1.94 1.3103 5 1 5 4 74.26 1.24 1.2772 6 2 4 4 74.40 4.09 1.2750 8 0 5 2 76.45 2.08 1.2459 -5 1 2 4 76.85 1.21 1.2405 -1 1 4 4 77.17 4.22 1.2361 8 0 0 2 81.01 4.74 1.1869 5 3 2 4 81.62 3.72 1.1796 5 3 1 4 81.62 9.18 1.1796 -3 3 1 4 81.88 9.11 1.1765 3 3 3 4 82.72 1.53 1.1666 9 -1 1 4 82.79 1.32 1.1658 8 -2 4 4 82.80 8.51 1.1658 0 2 4 4 82.96 2.13 1.1639 -6 0 2 2 83.50 1.93 1.1578 9 -1 5 4 83.51 2.03 1.1577 1 1 5 4 84.41 1.52 1.1476 8 -2 1 4 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.