Pd20Sb7 Wopersnow W, Schubert K Journal of the Less-Common Metals 51 (1977) 35-44 Kristallstrukturen von Pd20Sb7 und Pd20Te7 Note: isotypic with keithconnite _database_code_amcsd 0014139 CELL PARAMETERS: 11.7340 11.7340 11.0210 90.000 90.000 120.000 SPACE GROUP: R-3 X-RAY WAVELENGTH: 1.541838 Cell Volume: 1314.147 Density (g/cm3): 11.298 MAX. ABS. INTENSITY / VOLUME**2: 302.0978906 RIR: 8.707 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 24.23 1.27 3.6737 0 0 3 2 24.54 1.74 3.6269 2 1 1 6 28.32 1.37 3.1510 1 2 2 6 30.47 4.56 2.9335 2 2 0 6 35.78 9.31 2.5093 4 -1 2 6 36.07 1.33 2.4903 0 3 3 6 36.07 4.75 2.4903 3 0 3 6 36.29 5.61 2.4756 4 0 1 6 37.12 16.52 2.4221 0 2 4 6 39.04 11.63 2.3071 0 4 2 6 39.30 2.29 2.2923 4 -2 3 6 39.30 3.72 2.2923 2 2 3 6 39.51 1.52 2.2808 5 -2 1 6 39.51 4.73 2.2808 3 2 1 6 40.28 62.02 2.2388 2 1 4 6 40.28 24.85 2.2388 3 -1 4 6 40.69 99.85 2.2175 1 4 0 6 41.94 1.21 2.1541 0 1 5 6 42.08 5.89 2.1471 -2 5 2 6 44.82 3.29 2.0221 2 0 5 6 46.07 14.42 1.9702 -1 4 4 6 47.56 3.46 1.9118 -1 3 5 6 47.92 3.25 1.8985 1 4 3 6 47.92 3.16 1.8985 5 -1 3 6 48.09 2.32 1.8919 -2 6 1 6 48.76 1.18 1.8677 4 0 4 6 50.32 1.27 1.8135 6 -2 2 6 51.34 4.81 1.7797 3 2 4 6 52.18 1.73 1.7529 1 1 6 6 52.84 1.07 1.7326 1 5 2 6 53.05 1.46 1.7263 3 3 3 6 58.59 11.83 1.5755 -2 6 4 6 60.88 1.02 1.5216 5 1 4 6 62.23 1.00 1.4918 6 1 2 6 62.42 1.58 1.4878 -2 7 3 6 64.34 1.78 1.4480 4 2 5 6 64.77 1.40 1.4393 -3 8 1 6 64.77 1.36 1.4393 3 5 1 6 64.77 1.39 1.4393 7 0 1 6 65.32 5.47 1.4285 4 3 4 6 65.32 1.37 1.4285 7 -3 4 6 66.51 1.17 1.4058 -1 6 5 6 66.62 6.20 1.4038 5 3 2 6 68.77 2.62 1.3651 0 1 8 6 69.61 3.44 1.3507 -1 7 4 6 70.76 1.79 1.3314 3 4 5 6 70.87 2.97 1.3296 2 0 8 6 72.96 4.10 1.2967 1 2 8 6 72.96 3.94 1.2967 -1 3 8 6 73.78 1.15 1.2843 -3 8 4 6 73.78 4.86 1.2843 3 5 4 6 73.78 4.97 1.2843 7 0 4 6 74.05 8.76 1.2803 6 3 0 6 74.91 3.46 1.2677 7 -1 5 6 75.83 3.60 1.2546 8 -2 4 6 76.51 2.55 1.2451 6 0 6 6 77.05 2.58 1.2377 3 1 8 6 78.53 2.86 1.2180 2 5 6 6 78.53 1.03 1.2180 -2 7 6 6 78.97 2.01 1.2124 0 7 5 6 78.97 1.96 1.2124 8 -3 5 6 79.07 1.50 1.2111 9 -2 2 6 79.07 1.30 1.2110 0 4 8 6 79.24 2.25 1.2090 -3 9 3 6 79.24 1.64 1.2090 6 3 3 6 81.08 4.01 1.1860 -2 5 8 6 83.07 1.22 1.1626 -1 9 2 6 83.07 2.50 1.1626 1 8 2 6 83.87 1.27 1.1536 0 8 4 6 85.07 1.36 1.1403 5 0 8 6 87.05 2.40 1.1194 4 2 8 6 88.10 1.55 1.1088 2 8 0 6 89.03 1.07 1.0996 1 5 8 6 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.