Pd2PbBi Mayer H W, Bhatt Y C, Schubert K Journal of the Less-Common Metals 66 (1979) 1-9 Kristallstrukturen von Pd2PbBi und Pd4PbBi3 _database_code_amcsd 0014144 CELL PARAMETERS: 7.1710 8.6770 5.5750 90.000 71.740 90.000 SPACE GROUP: Cm X-RAY WAVELENGTH: 1.541838 Cell Volume: 329.424 Density (g/cm3): 12.681 MAX. ABS. INTENSITY / VOLUME**2: 252.6914613 RIR: 6.488 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 26.17 1.98 3.4050 2 0 0 1 26.31 4.50 3.3870 2 0 1 1 26.43 2.11 3.3728 -1 1 1 2 26.56 36.22 3.3557 0 2 1 2 33.45 100.00 2.6785 2 2 0 2 33.57 85.87 2.6698 2 2 1 2 33.67 11.51 2.6622 1 3 0 2 33.86 63.38 2.6471 0 0 2 1 35.54 29.57 2.5262 -2 0 1 1 35.85 5.41 2.5047 1 3 1 2 35.86 27.29 2.5044 2 0 2 1 39.37 5.91 2.2888 3 1 1 2 39.72 3.07 2.2695 -1 3 1 2 39.89 39.93 2.2597 0 2 2 2 41.10 2.50 2.1961 3 1 0 2 41.36 37.15 2.1831 -2 2 1 2 41.63 49.01 2.1693 0 4 0 2 41.64 46.07 2.1690 2 2 2 2 44.94 2.13 2.0171 3 1 2 2 45.25 2.93 2.0038 1 3 2 2 49.52 3.52 1.8406 -3 1 1 2 50.94 23.54 1.7927 4 0 1 1 51.59 2.93 1.7717 -1 3 2 2 54.40 10.91 1.6864 -2 2 2 2 54.57 1.80 1.6817 1 5 0 2 54.71 23.90 1.6778 0 4 2 2 54.79 9.82 1.6756 2 2 3 2 55.86 11.31 1.6458 -2 4 1 2 56.09 1.37 1.6398 1 5 1 2 56.09 10.65 1.6397 2 4 2 2 56.28 9.23 1.6347 0 2 3 2 58.21 5.59 1.5848 4 2 0 2 58.48 2.16 1.5783 -3 3 1 2 58.51 6.01 1.5776 4 2 2 2 58.89 1.98 1.5681 -1 5 1 2 62.30 6.86 1.4904 -4 0 1 1 62.86 8.29 1.4784 4 0 3 1 63.17 1.91 1.4719 1 5 2 2 64.44 1.25 1.4460 3 3 3 2 66.32 6.35 1.4095 -4 2 1 2 66.78 3.90 1.4008 3 5 1 2 66.86 4.12 1.3994 4 2 3 2 66.93 8.86 1.3980 -2 0 3 1 67.40 9.34 1.3894 2 0 4 1 67.82 14.76 1.3819 4 4 1 2 68.00 2.06 1.3787 3 5 0 2 70.78 6.41 1.3311 2 6 0 2 70.79 1.80 1.3309 3 5 2 2 70.85 5.55 1.3300 2 6 1 2 71.27 1.04 1.3232 2 2 4 2 73.86 2.78 1.2831 5 3 1 2 74.32 2.27 1.2763 -3 5 1 2 74.81 4.06 1.2691 0 6 2 2 75.03 9.60 1.2660 0 2 4 2 75.79 3.99 1.2551 -2 6 1 2 75.99 5.04 1.2524 2 6 2 2 77.75 5.22 1.2284 -4 4 1 2 78.25 6.46 1.2217 4 4 3 2 78.42 2.07 1.2195 1 7 0 2 78.94 2.52 1.2128 -4 2 2 2 79.69 1.12 1.2033 1 7 1 2 79.70 3.46 1.2031 4 2 4 2 81.64 1.07 1.1793 5 3 3 2 82.00 7.58 1.1751 -2 4 3 2 82.18 1.44 1.1729 -1 5 3 2 82.44 8.12 1.1700 2 4 4 2 84.51 3.93 1.1465 6 2 1 2 84.70 3.12 1.1444 6 2 2 2 85.57 2.18 1.1350 6 0 0 1 85.59 1.30 1.1347 -2 6 2 2 85.84 1.25 1.1320 1 7 2 2 85.90 1.19 1.1314 2 6 3 2 85.90 1.24 1.1314 -5 3 1 2 86.13 1.36 1.1290 6 0 3 1 86.58 1.78 1.1243 -3 3 3 2 87.13 1.35 1.1186 0 6 3 2 89.19 1.02 1.0980 6 2 0 2 89.75 2.49 1.0926 6 2 3 2 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.