D3.6 Th Zr2 Bartscher W, Rebizant J, Boeuf A, Caciuffo R, Rustichelli F, Fournier J, Kuhs W Journal of the Less-Common Metals 121 (1986) 455-460 Distribution of deuterium in the cubic Laves phases Th Zr2 Dx _cod_database_code 1008698 _database_code_amcsd 0016584 CELL PARAMETERS: 9.0420 9.0420 9.0420 90.000 90.000 90.000 SPACE GROUP: Fd3m X-RAY WAVELENGTH: 1.541838 Cell Volume: 739.254 Density (g/cm3): 7.512 MAX. ABS. INTENSITY / VOLUME**2: 421.7388852 RIR: 18.279 RIR based on corundum from Acta Crystallographica A38 (1982) 733-739 2-THETA INTENSITY D-SPACING H K L Multiplicity 16.98 9.98 5.2204 1 1 1 8 27.91 59.91 3.1968 2 2 0 12 32.85 100.00 2.7263 3 1 1 24 34.36 16.55 2.6102 2 2 2 8 43.63 2.75 2.0744 3 3 1 24 49.38 23.05 1.8457 4 2 2 24 52.59 24.07 1.7401 5 1 1 24 52.59 8.01 1.7401 3 3 3 8 57.67 23.36 1.5984 4 4 0 12 60.58 1.83 1.5284 5 3 1 48 65.26 8.87 1.4297 6 2 0 24 67.99 9.87 1.3789 5 3 3 24 68.88 5.29 1.3631 6 2 2 24 79.29 9.24 1.2083 6 4 2 48 81.82 5.38 1.1772 5 5 3 24 81.82 10.76 1.1772 7 3 1 48 86.01 3.12 1.1302 8 0 0 6 ================================================================================ XPOW Copyright 1993 Bob Downs, Ranjini Swaminathan and Kurt Bartelmehs For reference, see Downs et al. (1993) American Mineralogist 78, 1104-1107.